Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GN-3610L TEIJIN JAPAN
PANLITE®
machine,Mechanical components
High rigidity,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 45 kJ/m² |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3800 Mpa | |
| bending strength | ASTM D790/ISO 178 | 115 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 断裂 | ISO 527-2/5 | 70.0 Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 3600 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 115 Mpa | |
| Flexural modulus | ISO 178 | 3600 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| Tensile modulus | ASTM D638/ISO 527 | 3800 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 2.0 % | |
| tensile strength | ASTM D638/ISO 527 | 70.0 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| dielectric constant | 100Hz | IEC 60250 | 3.20 |
| Surface Resistivity | ASTM D257/IEC 60093 | 1.0E+15 Ω | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| dielectric constant | ASTM D150/IEC 60250 | 3.20 | |
| Dielectric loss | ASTM D150/IEC 60250 | 0.0090 | |
| dielectric constant | 1MHz | IEC 60250 | 3.20 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Volume resistivity | ASTM D257/IEC 60093 | 1.0E+15 Ω.cm | |
| Dissipation Factor | 1MHz | IEC 60250 | 9E-03 |
| other | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| notes | 以上加工数据.为参考值.以生产厂商设备的实际状况而进行调整。 |
| Physical properties | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.40-0.60 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.16 % |
| flammability | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 960 °C |
| 3.0mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 850 °C |
| 1.0mm | IEC 60695-2-13 | 825 °C | |
| UL flame retardant rating | 1.0mm | UL 94 | V-1 |
| Hot filament ignition temperature | 1.6mm | IEC 60695-2-13 | 850 °C |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| 0.40mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.16 % |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.30-0.50 % |
| TD:4.00mm | 内部方法 | 0.40-0.60 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/GN-3610L |
|---|---|---|---|
| RTI Imp | 1.5mm | UL 746 | 80.0 °C |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 143 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 146 ℃（℉） | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 143 °C |
| vicat | ISO 306/B50 | 146 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 140 °C |
| RTI Str | 1.5mm | UL 746 | 80.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4E-05 cm/cm/°C |
| RTI Elec | 1.5mm | UL 746 | 80.0 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 6E-05 cm/cm/°C |
| ASTM D696/ISO 11359 | 0.000060 mm/mm.℃ |