PC/PBT X4820 SABIC INNOVATIVE US
XENOY™ 
Automotive Applications
High mobility,High impact resistance,Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/X4820
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D64898.0 °C
1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af94.0 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8317.5E-05 cm/cm/°C
TD：-40to40°CISO 11359-21.1E-04 cm/cm/°C
TD：-40to40°CASTME8311.1E-04 cm/cm/°C
MD：-40to40°CISO 11359-27.5E-05 cm/cm/°C
Vicat softening temperature--ISO 306/B120134 °C
ASTM D152510130 °C
--ISO 306/B50132 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/X4820
Bending modulus50.0mmSpanASTM D7902900 Mpa
ISO 1782850 Mpa
bending strengthYield,50.0mmSpanASTM D79091.0 Mpa
ISO 17887.0 Mpa
elongationBreakASTM D638140 %
YieldASTM D6384.2 %
Tensile modulusASTM D6383200 Mpa
ISO 527-2/13000 Mpa
Tensile strainBreakISO 527-2/50100 %
YieldISO 527-2/504.2 %
tensile strengthYieldASTM D63857.0 Mpa
YieldISO 527-2/5058.0 Mpa
BreakISO 527-2/5052.0 Mpa
BreakASTM D63858.0 Mpa
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/X4820
melt mass-flow rate250°C/5.0kgASTM D123810 g/10min
Melt Volume Flow Rate (MVR)265°C/5.0kgISO 113312.0 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.95-1.1 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.14 %
Saturation,23°CISO 620.42 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/X4820
Charpy Notched Impact Strength23°CISO 179/1eA60 kJ/m²
Dart impact23°C,TotalEnergyASTM D376360.0 J
Impact strength of cantilever beam gap-30°CISO 180/1A15 kJ/m²
23°CISO 180/1A55 kJ/m²