Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 HTNFR52G30NHF BK337 DUPONT SHENZHEN
Zytel® 
Automotive sector,Electrical appliances,Electronic field,Electrical field
High temperature resistan,Flame retardant,Thermal stability,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Supplementary InformationTest ConditionTest MethodDUPONT SHENZHEN/HTNFR52G30NHF BK337
OdorVDA2703.50
Electrical performanceTest ConditionTest MethodDUPONT SHENZHEN/HTNFR52G30NHF BK337
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 0
dielectric strengthIEC 60243-133 KV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
relative permittivity100HzIEC 602504.30
Dissipation Factor100HzIEC 602507E-03
relative permittivity1MHzIEC 602504.00
Dissipation Factor1MHzIEC 602500.013
Mechanical propertiesTest ConditionTest MethodDUPONT SHENZHEN/HTNFR52G30NHF BK337
Tensile modulusISO 527-210000 Mpa
bending strengthISO 178230 Mpa
Tensile strain断裂ISO 527-22.2 %
Flexural modulusISO 1788700 Mpa
tensile strength 断裂ISO 527-2150 Mpa
flammabilityTest ConditionTest MethodDUPONT SHENZHEN/HTNFR52G30NHF BK337
UL flame retardant rating0.75mmUL 94V-0
0.75mmIEC 60695-11-10,-20V-0
1.5mmIEC 60695-11-10,-20V-0
Hot filament ignition temperature3.0mmIEC 60695-2-13775 °C
FMVSS flammabilityFMVSS302DNI
Hot filament ignition temperature0.40mmIEC 60695-2-13700 °C
UL flame retardant rating1.5mmUL 94V-0
Limiting Oxygen IndexISO 4589-237 %
Hot filament ignition temperature0.75mmIEC 60695-2-13725 °C
physical property Test ConditionTest MethodDUPONT SHENZHEN/HTNFR52G30NHF BK337
Shrinkage rateTDISO 294-41.0 %
MDISO 294-40.30 %
Thermal performanceTest ConditionTest MethodDUPONT SHENZHEN/HTNFR52G30NHF BK337
melting temperatureISO 11357-3310 °C
Heat distortion temperature1.8MPa,未退火,HDTISO 75-2/A283 °C
RTI Elec1.5mmUL 746140 °C
0.40mmUL 746140 °C
3.0mmUL 746140 °C
0.75mmUL 746140 °C