Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LB-1010W Samsung Cheil South Korea
INFINO®
LCD application
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/LB-1010W |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 47 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 370 J/m |
| 23°C | ISO 180/1A | 43 kJ/m² | |
| 23°C,3.18mm | ASTM D256 | 490 J/m |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/LB-1010W |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 116 |
| R级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/LB-1010W |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2200 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| elongation | 断裂 | ASTM D638 | 80 % |
| Tensile modulus | ISO 527-2/50 | 2100 Mpa | |
| bending strength | ISO 178 | 82.0 Mpa | |
| Flexural modulus | ISO 178 | 2200 Mpa | |
| bending strength | ASTM D790 | 77.0 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 58.0 Mpa |
| 屈服 | ASTM D638 | 52.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 87 % |
| Flexural modulus | ASTM D790 | 2100 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 55.0 Mpa |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/LB-1010W |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/LB-1010W |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.50-0.70 % |
| density | ASTM D792 | 1.26 g/cm³ | |
| melt mass-flow rate | 250°C/10.0kg | ASTM D1238 | 48 g/10min |
| density | ISO 1183 | 1.26 g/cm³ | |
| melt mass-flow rate | 250°C/10.0kg | ISO 1133 | 48 g/10min |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/LB-1010W |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 117 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 129 °C | |
| vicat | -- | ISO 306/B120 | 141 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 132 °C |
| 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 123 °C | |
| vicat | -- | ISO 306/B50 | 139 °C |
| Heat distortion temperature | 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 133 °C |