PC GP1000M LG CHEM KOREA
LUPOY®
Automotive interior parts、Electronic field、Electrical field、Electrical/Electronic App、Automotive External Parts
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | LG CHEM KOREA/GP1000M |
---|---|---|---|
Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 740 J/m |
hardness | Test Condition | Test Method | LG CHEM KOREA/GP1000M |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 118 |
Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/GP1000M |
---|---|---|---|
elongation | 断裂,3.20mm | ASTM D638 | >150 % |
tensile strength | 屈服,3.20mm | ASTM D638 | 61.8 Mpa |
Flexural modulus | 3.20mm | ASTM D790 | 2260 Mpa |
bending strength | 屈服,3.20mm | ASTM D790 | 98.1 Mpa |
Electrical performance | Test Condition | Test Method | LG CHEM KOREA/GP1000M |
---|---|---|---|
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
Volume resistivity | 23°C | ASTM D257 | 2E+17 ohms·cm |
dielectric strength | 23°C,1.00mm | ASTM D149 | 17 KV/mm |
flammability | Test Condition | Test Method | LG CHEM KOREA/GP1000M |
---|---|---|---|
UL flame retardant rating | 3.0mm | UL 94 | HB |
1.5mm | UL 94 | HB |
physical property | Test Condition | Test Method | LG CHEM KOREA/GP1000M |
---|---|---|---|
Shrinkage rate | MD:3.20mm | ASTM D955 | 0.50-0.80 % |
density | ASTM D792 | 1.20 g/cm³ | |
melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 11 g/10min |
Thermal performance | Test Condition | Test Method | LG CHEM KOREA/GP1000M |
---|---|---|---|
vicat | ASTM D15255 | 141 °C | |
Heat distortion temperature | 0.45MPa,未退火,6.40mm,HDT | ASTM D648 | 130 °C |
RTI Imp | UL 746 | 130 °C | |
RTI Str | UL 746 | 130 °C | |
RTI Elec | UL 746 | 130 °C |