PC+ABS RAMLLOY PBB104 POLYRAM ISRAEL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYRAM ISRAEL/RAMLLOY PBB104 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 500 J/m |
| 23°C | ISO 180 | 30 kJ/m² |
| Mechanical properties | Test Condition | Test Method | POLYRAM ISRAEL/RAMLLOY PBB104 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | >30 % |
| Tensile modulus | ASTM D638 | 2200 MPa | |
| ISO 527-2 | 2200 MPa | ||
| Tensile strain | 断裂 | ISO 527-2 | >30 % |
| tensile strength | 屈服 | ISO 527-2 | 50.0 MPa |
| 屈服 | ASTM D638 | 50.0 MPa |
| Electrical performance | Test Condition | Test Method | POLYRAM ISRAEL/RAMLLOY PBB104 |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+14 ohms |
| flammability | Test Condition | Test Method | POLYRAM ISRAEL/RAMLLOY PBB104 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| physical property | Test Condition | Test Method | POLYRAM ISRAEL/RAMLLOY PBB104 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 0.40to0.70 % | |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 30 g/10min |
| Shrinkage rate | MD | 0.40to0.70 % | |
| density | ASTM D792 | 1.13 g/cm³ | |
| ISO 1183 | 1.13 g/cm³ | ||
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 30 g/10min |
| Thermal performance | Test Condition | Test Method | POLYRAM ISRAEL/RAMLLOY PBB104 |
|---|---|---|---|
| vicat | ASTM D1525 | 116 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 100 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 120 °C | |
| vicat | ISO 306 | 116 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 120 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 100 °C |