Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 500 BK602 DUPONT USA
Delrin®
Automotive Applications、Fitness equipment、Engine parts
High rigidity、heat-resisting、High impact resistance、Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | DUPONT USA/500 BK602 |
|---|---|---|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1.1E-04 cm/cm/°C |
| Annealing Time-Optional | 30.0 min/mm | ||
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 158 °C |
| 1.8MPa,未退火 | ISO75-2/A | 90.0 °C | |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 1.1E-04 cm/cm/°C |
| Melting Temperature | ISO11357-3 | 178 °C | |
| Annealing Temperature | 160 °C | ||
| Vicat Softening Temperature | ISO306/B50 | 160 °C |
| Hardness | Test Condition | Test Method | DUPONT USA/500 BK602 |
|---|---|---|---|
| Rockwell Hardness | M计秤 | ISO2039-2 | 92 |
| R计秤 | ISO2039-2 | 120 |
| Additional | Test Condition | Test Method | DUPONT USA/500 BK602 |
|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 6.00 µgC/g | |
| Emission | VDA275 | <8.00 mg/kg |
| Mechanical Properties | Test Condition | Test Method | DUPONT USA/500 BK602 |
|---|---|---|---|
| Flexural Modulus | ISO178 | 2900 Mpa | |
| Tensile Strain | 屈服 | ISO527-2 | 15 % |
| Tensile Stress | 屈服 | ISO527-2 | 67.0 Mpa |
| Nominal Tensile Strain at Break | ISO527-2 | 25 % | |
| Tensile Modulus | ISO527-2 | 3100 Mpa |
| Physical | Test Condition | Test Method | DUPONT USA/500 BK602 |
|---|---|---|---|
| Density / Specific Gravity | ISO1183 | 1.41 g/cm³ | |
| Moisture Absorption | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.25 % |
| Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 12.0 cm3/10min |
| Moisture Absorption | 饱和,23°C,2.00mm | ISO62 | 1.0 % |
| Melt Mass-Flow Rate | ISO1133 | 15 g/10min | |
| Modeling Shrinkage | TD | ISO294-4 | 1.8 % |
| MD | ISO294-4 | 1.9 % |
| Impact Properties | Test Condition | Test Method | DUPONT USA/500 BK602 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 350 kJ/m² |
| Notched Izod Impact Strength | -40°C | ISO180/1A | 9.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7.0 kJ/m² |
| 23°C | ISO179/1eA | 8.0 kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 290 kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 9.0 kJ/m² |
| Flammability | Test Condition | Test Method | DUPONT USA/500 BK602 |
|---|---|---|---|
| Burning Rate | 1.00mm | ISO3795 | 28 mm/min |
| Flame Rating | 0.75mm | IEC60695-11-10,-20 | HB |
| 1.5mm | IEC60695-11-10,-20 | HB | |
| 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | |
| FMVSS Flammability | FMVSS302 | B |
| Electrical Properties | Test Condition | Test Method | DUPONT USA/500 BK602 |
|---|---|---|---|
| Relative Permittivity | 100Hz | IEC60250 | 4.20 |
| Comparative Tracking Index | IEC60112 | 600 V | |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Relative Permittivity | 1MHz | IEC60250 | 4.10 |