PC/ABS M130-S MARPLEX AUSTRALIA
--
Automotive sector、Automotive External Parts
High impact resistance、Moderate heat resistance、Easy to process、Good impact resistance、High mobility、Moderate heat resistance、Medium hardness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | MARPLEX AUSTRALIA/M130-S |
|---|---|---|---|
| UL flame retardant rating | 1.60mm | UL 94 | HB |
| Basic performance | Test Condition | Test Method | MARPLEX AUSTRALIA/M130-S |
|---|---|---|---|
| Shrinkage rate | 流动,3.00mm | ASTM D-955 | 0.4-0.8 % |
| Water absorption rate | 24hr | ASTM D-570 | 0.25 % |
| melt mass-flow rate | 250℃/3.8kg | ASTM D-1238 | 12 g/10min |
| density | ASTM D-792 | 1.12 g/cm³ |
| Mechanical properties | Test Condition | Test Method | MARPLEX AUSTRALIA/M130-S |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.20mm | ASTM D-256 | 625 J/m |
| Rockwell hardness | R | ASTM D-785 | 116 |
| Flexural modulus | 3.20mm | ASTM D-790 | 2450 Mpa |
| tensile strength | 3.20mm | ASTM D-638 | 56 Mpa |
| bending strength | 3.20mm | ASTM D-790 | 86 Mpa |
| elongation | 断裂,3.20mm | ASTM D-638 | 100 % |
| Dart impact | 3.20mm | ASTM D-3029 | 55 J |
| Thermal performance | Test Condition | Test Method | MARPLEX AUSTRALIA/M130-S |
|---|---|---|---|
| Hot filament point temperature | 1.60mm | AS/NS 60695.2.12 | 550 °C |
| vicat | ASTM D-1525 | 138 °C | |
| Heat distortion temperature | 1.8MPa,未退火,6.4mm，HDT | ASTM D-648 | 108 °C |
| Linear expansion coefficient | 流动 | ASTM D-696 | 0.000072 cm/cm/℃ |
| Heat distortion temperature | 1.8MPa,未退火,3.2mm，HDT | ASTM D-648 | 102 °C |
| 1.8MPa,未退火,12.7mm，HDT | ASTM D-648 | 113 °C |