POM 500P DUPONT SHENZHEN
Delrin®
Automotive sector、Fitness equipment
High rigidity、Aging resistance、currency、Weather resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT SHENZHEN/500P |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 8.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 180 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 160 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT SHENZHEN/500P |
|---|---|---|---|
| Emission | VDA275 | <8.00 mg/kg | |
| Emissions of Organic Compounds | VDA277 | 3.10 µgC/g |
| Electrical performance | Test Condition | Test Method | DUPONT SHENZHEN/500P |
|---|---|---|---|
| CTI | IEC60112 | 600 V |
| Mechanical properties | Test Condition | Test Method | DUPONT SHENZHEN/500P |
|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 25 % | |
| Tensile stress | 屈服 | ISO527-2 | 71.0 Mpa |
| Tensile strain | 屈服 | ISO527-2 | 14 % |
| Tensile modulus | ISO527-2 | 3100 Mpa | |
| Flexural modulus | ISO178 | 3000 Mpa | |
| Poisson's ratio | ISO527 | 0.35 |
| flammability | Test Condition | Test Method | DUPONT SHENZHEN/500P |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
| atomization | F-value(refraction) | ISO6452 | 90 % |
| FMVSS flammability | FMVSS302 | B | |
| Burning rate 3 | 1.00mm | ISO3795 | 24 mm/min |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB |
| 0.8mm | UL94 | HB | |
| atomization | G-value(condensate) | ISO6452 | 3.5E-04 g |
| UL flame retardant rating | 0.8mm | IEC60695-11-10,-20 | HB |
| physical property | Test Condition | Test Method | DUPONT SHENZHEN/500P |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.8 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 1.3 % |
| melt mass-flow rate | 190°C/2.16kg | ISO1133 | 15 g/10min |
| Shrinkage rate | MD | ISO294-4 | 2.0 % |
| density | ISO1183 | 1.42 g/cm³ | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.40 % |
| Thermal performance | Test Condition | Test Method | DUPONT SHENZHEN/500P |
|---|---|---|---|
| MD：-40to23°C | ISO11359-2 | 9E-05 cm/cm/°C | |
| 0.45MPa,未退火 | ISO75-2/B | 162 °C | |
| TD：-- | ISO11359-2 | 1E-04 cm/cm/°C | |
| 1.8MPa,未退火 | ISO75-2/A | 96.0 °C | |
| melting temperature | ISO11357-3 | 178 °C | |
| Linear coefficient of thermal expansion | TD：AnnealingTime-Optional | ISO11359-2 | 30.0 min/mm |
| MD：-- | ISO11359-2 | 1E-04 cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 9E-05 cm/cm/°C | |
| Linear coefficient of thermal expansion | TD：AnnealingTemperature | ISO11359-2 | 160 °C |