PBT 330HR-ED3002 JAPAN POLYPLASTIC
DURANEX®
Automotive Applications
Hydrolysis resistance,30%GF,Filler: Glass fiber reinf,30%,Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/330HR-ED3002 |
|---|---|---|---|
| ColorNumber | EF2001/ED3002 |
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/330HR-ED3002 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 100 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/330HR-ED3002 |
|---|---|---|---|
| tensile strength | ISO 527-1/-2 | 149 Mpa | |
| bending strength | ISO 178 | 230 Mpa | |
| Flexural modulus | ISO 178 | 9100 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.6 % |
| Charpy Notched Impact Strength | ISO 179/1eA | 11.0 KJ/m | |
| tensile strength | ISO 527-2 | 149 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/330HR-ED3002 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 2E+16 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 26 KV/mm |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/330HR-ED3002 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/330HR-ED3002 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/330HR-ED3002 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 9E-05 cm/cm/°C |
| Heat distortion temperature | 1.8Mpa，HDT | ISO 75-1/-2 | 209 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | 内部方法 | 2E-05 cm/cm/°C |
| 垂直方向 | ISO 11359-2 | 9 | |
| 流动方向 | ISO 11359-2 | 2 | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 209 °C |
| UL flame retardant rating | UL 94 | HB |