Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM F20-73R1 MITSUBISHI THAILAND
Iupital™
Electronic and Electrical、Automotive sector
Weather resistance、Medium viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI THAILAND/F20-73R1 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 250 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 7.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI THAILAND/F20-73R1 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 30 % | |
| Tensile stress | 屈服 | ISO527-2 | 65.0 Mpa |
| Tensile strain | 屈服 | ISO527-2 | 8.5 % |
| Bending stress | ISO178 | 91.0 Mpa | |
| Tensile modulus | ISO527-2 | 2900 Mpa | |
| Flexural modulus | ISO178 | 2610 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI THAILAND/F20-73R1 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+16 ohms | |
| Volume resistivity | IEC60093 | 1E+14 ohms·cm |
| flammability | Test Condition | Test Method | MITSUBISHI THAILAND/F20-73R1 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB |
| physical property | Test Condition | Test Method | MITSUBISHI THAILAND/F20-73R1 |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm | 2.0 % | |
| melt mass-flow rate | 190°C/2.16kg | ISO1133 | 9.1 g/10min |
| Water absorption rate 2 | 平衡,23°C,50%RH | ISO62 | 0.22 % |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 7.90 cm3/10min |
| density | ISO1183 | 1.41 g/cm³ | |
| Shrinkage rate | MD:3.00mm | 2.0 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI THAILAND/F20-73R1 |
|---|---|---|---|
| TD | ISO11359-2 | 1.1E-04 cm/cm/°C | |
| 0.45MPa,未退火 | ISO75-2/B | 160 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 100 °C | |
| melting temperature | ISO11357-3 | 166 °C | |
| MD | ISO11359-2 | 1.1E-04 cm/cm/°C |