PMMA LG702 Lucite (Taiwan)
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | Lucite (Taiwan)/LG702 |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 7.3 g/10min | |
| density | ISO 1183 | 1.18 g/cm | |
| Water absorption rate | Equilibrium,23℃,50% RH | ISO 62 | 0.3 % |
| Mechanical properties | Test Condition | Test Method | Lucite (Taiwan)/LG702 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/1A | 1.8 KJ/m | |
| Tensile stress | 屈服 | ISO 527-2 | 80 MPa |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 20 KJ/m | |
| Tensile strain | 屈服 | ISO 527-2 | 5 % |
| Charpy Notched Impact Strength | ISO 179/1eA | 2 KJ/m | |
| Flexural modulus | ISO 178 | 3000 MPa | |
| Impact energy of dual axis instruments | ISO 6603-2 | 0.3 J | |
| bending strength | ISO 178 | 110 MPa |
| optical performance | Test Condition | Test Method | Lucite (Taiwan)/LG702 |
|---|---|---|---|
| transmittance | ASTM D1003 | 92 % | |
| Haze ratio | ASTM D1003 | 0.4 % | |
| refractive index | ISO 489 | 1.49 |
| physical property | Test Condition | Test Method | Lucite (Taiwan)/LG702 |
|---|---|---|---|
| Rockwell hardness | M-Scale | ISO 2039-2 | 92 |
| ball-indentation hardness | ISO 2039-1 | 180 MPa |
| Thermal performance | Test Condition | Test Method | Lucite (Taiwan)/LG702 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2B | 100 ℃ |
| 1.8MPa,未退火，HDT | ISO 75-2A | 97 ℃ | |
| Linear coefficient of thermal expansion | 流动 | ASTM D696 | 0.000071 cm/cm/℃ |
| GWIT | IEC 60695-2-13 | 650 ℃ | |
| vicat | ISO 306A | 108 ℃ | |
| ISO 306B | 102 ℃ | ||
| UL flame retardant rating | UL 94 | HB |