Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC D2000 BK1A643 SABIC INNOVATIVE US
LNP™ LUBRILOY™
Electrical appliances、Plastic bag、Aerospace Applications
wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/D2000 BK1A643 |
|---|---|---|---|
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 7.4E-5 cm/cm/°C |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 4 | ISO 75-2/Bf | 140 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 4 | ISO 75-2/Af | 128 °C | |
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 7.4E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 7.4E-5 cm/cm/°C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 130 °C |
| 0.45 MPa, 未退火, 3.20 mm | 142 °C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/D2000 BK1A643 |
|---|---|---|---|
| Suggested Max Moisture | 0.020 % | ||
| Middle Temperature | 300 到 310 °C | ||
| Processing (Melt) Temp | 305 到 315 °C | ||
| Drying Time | 4.0 hr | ||
| Rear Temperature | 295 到 305 °C | ||
| Drying Temperature | 100 °C | ||
| Front Temperature | 305 到 315 °C | ||
| Back Pressure | 0.200 到 0.300 Mpa | ||
| Mold Temperature | 65 到 95 °C | ||
| Screw Speed | 30 到 60 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/D2000 BK1A643 |
|---|---|---|---|
| Modeling Shrinkage | 流动 : 24小时 | ASTM D955 | 0.70 到 0.90 % |
| Moisture Absorption | 24 hr, 50% RH | ASTM D570 | 0.14 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.18 % | |
| Modeling Shrinkage | 横向流动 : 24小时 | ASTM D955 | 0.70 到 0.90 % |
| 横向流量 : 24小时 | ISO 294-4 | 0.70 到 0.90 % | |
| 流量 : 24小时 | 0.70 到 0.90 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/D2000 BK1A643 |
|---|---|---|---|
| Tensile Elongation | 屈服 | ISO 527-2 | 5.6 % |
| Tensile Modulus | -- | ISO 527-2/1 | 2120 Mpa |
| Flexural Strength | ISO 178 | 78.0 Mpa | |
| Specific Wear Rate | ASTM D3702 | 1.2E+7 10^-8 mm³/N·m | |
| Flexural Strength | -- | ASTM D790 | 82.0 Mpa |
| Coefficient of Friction | Dynamic | ASTM D3702 | 0.16 |
| Tensile Strength | 断裂 | ISO 527-2 | 54.0 Mpa |
| ASTM D638 | 60.0 Mpa | ||
| Tensile Elongation | 130 % | ||
| Tensile Modulus | -- 2 | 1860 Mpa | |
| Tensile Elongation | 断裂 | ISO 527-2 | 99 % |
| Tensile Strength | 屈服 | ASTM D638 | 53.0 Mpa |
| ISO 527-2 | 51.0 Mpa | ||
| Tensile Elongation | ASTM D638 | 6.5 % | |
| Coefficient of Friction | Static | ASTM D3702 | 0.090 |
| Flexural Modulus | ASTM D790, ISO 178 | 2130 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/D2000 BK1A643 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 无断裂 |
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 40.0 J |
| -- | ISO 6603-2 | 45.0 J | |
| Unnotched Izod Impact Strength | 23°C 4 | ISO 180/1U | 140 kJ/m² |