PPA UL-4020 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Mechanical parts、consumer goods
Thermal stability、Carbon fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/UL-4020 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 27 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 2.80 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 0.500 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 2.7 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/UL-4020 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3220 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 60.0 Mpa |
| elongation | 屈服 | ASTM D638 | 2.2 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 2.2 % |
| Wear factor | Washer | ASTM D3702Modified | 20.0 10^-10in^5-min/ft-lb-hr |
| tensile strength | 断裂 | ASTM D638 | 60.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2980 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 58.0 Mpa |
| Tensile modulus | ASTM D638 | 3170 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.2 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 105 Mpa |
| coefficient of friction | Static | ASTM D3702Modified | 0.17 |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.2 % |
| Wear factor | Ring | ASTM D3702Modified | -0.100 10^-10in^5-min/ft-lb-hr |
| tensile strength | 屈服 | ASTM D638 | 60.0 Mpa |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.27 |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 105 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/UL-4020 |
|---|---|---|---|
| Shrinkage rate | MD：24小时 | ASTM D955 | 0.90-2.0 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.47 % |
| 平衡,23°C,50%RH | ISO 62 | 0.73 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.70-0.90 % |