Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DBL-4034 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Plastic bag
Easy to form,Flame retardant,Filler: Glass beads
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DBL-4034 |
|---|---|---|---|
| 0.45MPa, unannealed, 64.0mm span | ISO 75-2/Bf | 137 °C | |
| 1.8MPa, unannealed, 64.0mm span of | ISO 75-2/Af | 130 °C | |
| Linear coefficient of thermal expansion | TD:23到60°C | ISO 11359-2 | 6.9E-05 cm/cm/°C |
| MD:23到60°C | ISO 11359-2 | 6E-05 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DBL-4034 |
|---|---|---|---|
| Bending modulus | ISO 178 | 2900 Mpa | |
| bending strength | ISO 178 | 76.0 Mpa | |
| Fracture bending strain | ISO 178 | 5.3 % | |
| Friction coefficient | 与自身-动态 | ASTM D3702Modified | 0.50 |
| Tensile modulus | ISO 527-2/1 | 2800 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 4.6 % |
| 屈服 | ISO 527-2/5 | 3.1 % | |
| tensile strength | 断裂 | ISO 527-2/5 | 40.0 Mpa |
| 屈服 | ISO 527-2/5 | 42.0 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 94.0 10^-10in^5-min/ft-lb-hr |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DBL-4034 |
|---|---|---|---|
| Shrinkage rate | MD | Internal Method | 0.50-0.70 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.13 % |
| impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/DBL-4034 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 25 kJ/m² |