ABS Jamplast JPPCABS10 Jamplast, Inc.
--
--
Filler, glass fiber reinforced material, 10%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Jamplast, Inc./Jamplast JPPCABS10 |
|---|---|---|---|
| Dart impact | 23°C,3.18mm,PeakEnergy | ASTM D3763 | 12.4 J |
| Impact strength of cantilever beam gap | -29°C,3.18mm | ASTM D256 | 80 J/m |
| 23°C,3.18mm | ASTM D256 | 230 J/m | |
| Dart impact | -29°C,3.18mm,TotalEnergy | ASTM D3763 | 5.65 J |
| hardness | Test Condition | Test Method | Jamplast, Inc./Jamplast JPPCABS10 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | Jamplast, Inc./Jamplast JPPCABS10 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 4.0 % |
| bending strength | 屈服 | ASTM D790 | 98.6 MPa |
| tensile strength | 断裂 | ASTM D638 | 50.4 MPa |
| Flexural modulus | ASTM D790 | 3650 MPa | |
| tensile strength | 屈服 | ASTM D638 | 48.7 MPa |
| physical property | Test Condition | Test Method | Jamplast, Inc./Jamplast JPPCABS10 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40 % |
| Water absorption rate | 平衡,23°C,50%RH | ASTM D570 | 0.32 % |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 2.6 g/10min |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.15 % |
| density | ASTM D792 | 1.18 g/cm³ |
| Thermal performance | Test Condition | Test Method | Jamplast, Inc./Jamplast JPPCABS10 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 121 °C |
| Linear coefficient of thermal expansion | MD：-40到82°C | ASTM D696 | 5.8E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,退火,3.18mm，HDT | ASTM D648 | 127 °C |