Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DX11354X SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and Electrical、Plastic bag、LDS
High impact resistance、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DX11354X |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 117 °C | |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 121 °C | |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 6.5E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 7.1E-05 cm/cm/°C | |
| Vicat Softening Temperature | ISO306/B50,ASTMD152512 | 136 °C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/DX11354X |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.050 % |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 20.0 cm3/10min |
| Modeling Shrinkage | TD:24小时 | ISO294-4 | 0.50到0.70 % |
| MD:24小时 | ISO294-4 | 0.50到0.70 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DX11354X |
|---|---|---|---|
| ASTMD638 | 2400 Mpa | ||
| Break | ASTMD638 | 45.0 Mpa | |
| fracture | ISO527-2/50 | 84 % | |
| Break | ASTMD638 | 70 % | |
| Yield,50.0mm Span | ASTMD790 | 86.0 Mpa | |
| yield | ISO527-2/50 | 5.0 % | |
| Yield | ASTMD638 | 5.0 % | |
| 50.0mm Span | ASTMD790 | 2380 Mpa | |
| fracture | ISO527-2/50 | 51.0 Mpa | |
| ISO178 | 86.0 Mpa | ||
| Yield | ASTMD638 | 55.0 Mpa | |
| yield | ISO527-2/50 | 54.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DX11354X |
|---|---|---|---|
| ASTMD256 | 700 J/m | ||
| ISO180/1A | 60 kJ/m² |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DX11354X |
|---|---|---|---|
| Surface Resistivity | ASTMD257 | 1E+16 ohms | |
| Volume Resistivity | ASTMD257 | 1E+16 ohms·cm | |
| Dielectric Constant | 1.00GHz | ASTMD150 | 3.03 |
| Dissipation Factor? | 1.00GHz | ASTMD150 | 6.6E-03 |