Product Name / Manufacturer / Model

Grade

Reference Price

PPO SABIC INNOVATIVE SHANGHAI SE1X-111

Injection grade

US$ 4,410 / MT

FOB Shanghai port, China

injection	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/SE1X-111
Back pressure			0.300 to 0.700 Mpa
Temperature at the front of the material cylinder			270 to 310 °C
Spray nozzle temperature			280 to 310 °C
Screw speed			20 to 100 rpm
Mold temperature			75 to 105 °C
Processing (melt) temperature			280 to 310 °C
drying temperature			105 to 110 °C
Suggested injection volume			30 to 70 %
Temperature in the middle of the barrel			260 to 305 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			250 to 300 °C
mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/SE1X-111
elongation	Break	ASTM D638	20 %
bending strength	Yield, 100 mm Span	ASTM D790	102 Mpa
Bending modulus	100 mm Span	ASTM D790	2500 Mpa
tensile strength	Break	ASTM D638	53.0 Mpa
tensile strength		Yield	ASTM D638	67.0 Mpa
elongation	Yield	ASTM D638	8.1 %
Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/SE1X-111
Water absorption rate	24 hr	ASTM D570	0.060 %
Shrinkage rate	Across FlowFlow 2	Internal Method	0.50 - 0.70 %
Outdoor applicability		UL 746C	f1
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.70 %
thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/SE1X-111
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	126 °C
Hot deformation temperature		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	117 °C
RTI Elec		UL 746	110 °C
RTI Imp		UL 746	105 °C
RTI		UL 746	110 °C
flammability	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/SE1X-111
Radiation board grade			RP100
UL flame retardant rating	1.5 mm	UL 94	V-1
UL flame retardant rating		6.0 mm	UL 94	V-0
Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/SE1X-111
Compared to the anti leakage trace index		UL 746	PLC 1
Surface resistivity		ASTM D257	> 1.0E+15 ohms
Dielectric strength	3.20 mm, in Oil	ASTM D149	18 KV/mm
Dissipation factor	50 Hz	ASTM D150	3.4E-3
		60 Hz	ASTM D150	3.4E-3
		1 MHz	ASTM D150	2.1E-3
Volume resistivity		ASTM D257	2.3E+16 ohms·cm
High voltage arc tracing rate		UL 746	PLC 4
Arc resistance		ASTM D495	PLC 6
Dielectric constant	60 Hz	ASTM D150	2.52
		50 kHz	ASTM D150	2.52
		1 MHz	ASTM D150	2.46
impact performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/SE1X-111
Dart impact	-30°C, Energy at Peak	ASTM D3763	32.0 J
Dart impact		23°C, Energy at Peak	ASTM D3763	51.0 J