PA6 BFG10 ZIG SHENG TAIWAN
ZISAMIDE®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ZIG SHENG TAIWAN/BFG10 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | ZIG SHENG TAIWAN/BFG10 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 6000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 110 Mpa |
| bending strength | ISO 178 | 170 Mpa | |
| Flexural modulus | ISO 178 | 5000 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 4.0 % |
| flammability | Test Condition | Test Method | ZIG SHENG TAIWAN/BFG10 |
|---|---|---|---|
| UL flame retardant rating | 1.6 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ZIG SHENG TAIWAN/BFG10 |
|---|---|---|---|
| Shrinkage rate | 横向流量 : 80°C, 2.00 mm | ISO 294-4 | 0.90 % |
| 流量 : 80°C, 2.00 mm | ISO 294-4 | 0.50 % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 1.2 % |
| Thermal performance | Test Condition | Test Method | ZIG SHENG TAIWAN/BFG10 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 220 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 215 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 205 °C |
| injection | Test Condition | Test Method | ZIG SHENG TAIWAN/BFG10 |
|---|---|---|---|
| Processing (melt) temperature | 265 to 280 °C | ||
| drying temperature | 80 °C | ||
| Residual Moisture Content | Karl Fisher | < 0.10 % | |
| Drying time - vacuum dryer | 2.0 to 6.0 hr | ||
| Temperature | 80 to 120 °C |