Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 1132T BK SABIC INNOVATIVE US
LEXAN™
Lighting applications,Plastic bag
Middle flow,Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/1132T BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 65 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 74.9 J |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 45 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 40 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 55 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/1132T BK |
|---|---|---|---|
| Rockwell hardness | L计秤 | ISO 2039-2 | 89 |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/1132T BK |
|---|---|---|---|
| RTI Elec | UL 746 | 130 °C | |
| RTI Str | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO 11359-2 | 7.6E-05 cm/cm/°C |
| vicat | -- | ISO 306/B120 | 140 °C |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 7.5E-05 cm/cm/°C |
| MD：23到80°C | ISO 11359-2 | 7.5E-05 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 122 °C |
| vicat | -- | ISO 306/B50 | 139 °C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 117 °C |
| vicat | ASTM D152510 | 139 °C | |
| Linear coefficient of thermal expansion | TD：-40to95°C | ASTME831 | 7.6E-05 cm/cm/°C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/1132T BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2340 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 57.8 Mpa |
| 屈服 | ASTM D638 | 58.6 Mpa | |
| elongation | 屈服 | ASTM D638 | 5.7 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2250 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.4 % |
| Tensile modulus | ASTM D638 | 2260 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 56.8 Mpa |
| elongation | 断裂 | ASTM D638 | 120 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 94.8 Mpa |
| tensile strength | 断裂 | ASTM D638 | 57.1 Mpa |
| bending strength | ISO 178 | 89.5 Mpa | |
| flexural modulus | ISO 178 | 2150 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 120 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/1132T BK |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
| volume resistivity | ASTM D257 | >1.0E+15 ohms·cm |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/1132T BK |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 3.0 % |
| transmissivity | 2540µm | ASTM D1003 | 82.0 % |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/1132T BK |
|---|---|---|---|
| shrinkage rate | TD：3.20mm | 内部方法 | 0.40-0.80 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 19.0 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.12 % |
| 平衡,23°C,50%RH | ISO 62 | 0.090 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 20 g/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/1132T BK |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Hot filament ignition temperature | 0.8mm | IEC 60695-2-13 | 850 °C |