PC GV-3420R TEIJIN JAPAN
PANLITE®
Electrical applications、Casters
Glass fiber reinforced、Flame retardant、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTEIJIN JAPAN/GV-3420R
Impact strength of simply supported beam without notchISO 17935 kJ/m²
Mechanical propertiesTest ConditionTest MethodTEIJIN JAPAN/GV-3420R
Tensile modulusISO 527-2/16200 Mpa
bending strengthASTM D790/ISO 178140 kg/cm²(MPa)[Lb/in²]
tensile strength 断裂ISO 527-2/590.0 Mpa
Flexural modulusASTM D790/ISO 1785700 kg/cm²(MPa)[Lb/in²]
bending strengthISO 178140 Mpa
Flexural modulusISO 1785700 Mpa
Tensile strain断裂ISO 527-2/53.0 %
Tensile modulusASTM D638/ISO 5276200 kg/cm²(MPa)[Lb/in²]
tensile strength ASTM D638/ISO 52790.0 kg/cm²(MPa)[Lb/in²]
Electrical performanceTest ConditionTest MethodTEIJIN JAPAN/GV-3420R
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 3
dielectric constant100HzIEC 602503.40
Surface ResistivityASTM D257/IEC 600931.0E+15 Ω
dielectric strengthIEC 60243-135 KV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Dissipation Factor100HzIEC 602501E-03
dielectric constantASTM D150/IEC 602503.40
Dielectric lossASTM D150/IEC 602500.0090
dielectric constant1MHzIEC 602503.40
Surface ResistivityIEC 60093>1.0E+15 ohms
Volume resistivityASTM D257/IEC 600931.0E+15 Ω.cm
Dissipation Factor1MHzIEC 602509E-03
otherTest ConditionTest MethodTEIJIN JAPAN/GV-3420R
notes以上加工数据.为参考值.以生产厂商设备的实际状况而进行调整。
Physical propertiesTest ConditionTest MethodTEIJIN JAPAN/GV-3420R
Shrinkage rateASTM D9550.40-0.60 %
Water absorption rateASTM D570/ISO 620.14 %
flammabilityTest ConditionTest MethodTEIJIN JAPAN/GV-3420R
UL flame retardant rating0.75mmUL 94V-0
2.5mmUL 945VA
0.40mmUL 94V-2
physical property Test ConditionTest MethodTEIJIN JAPAN/GV-3420R
Water absorption rate23°C,24hrISO 620.14 %
Shrinkage rateMD:4.00mm内部方法0.10-0.30 %
TD:4.00mm内部方法0.40-0.60 %
Thermal performanceTest ConditionTest MethodTEIJIN JAPAN/GV-3420R
RTI Imp1.5mmUL 746120 °C
Heat distortion temperatureHDTASTM D648/ISO 75149 ℃（℉）
vicatASTM D1525/ISO R306151 ℃（℉）
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B149 °C
vicatISO 306/B50151 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A146 °C
RTI Str1.5mmUL 746130 °C
Linear coefficient of thermal expansionMDISO 11359-23E-05 cm/cm/°C
RTI Elec1.5mmUL 746130 °C
Linear coefficient of thermal expansionTDISO 11359-26E-05 cm/cm/°C
ASTM D696/ISO 113590.000030 mm/mm.℃