Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA XTWM206-BK1B069 SABIC INNOVATIVE US
GELOY™
Electronic and electrical、Lawn garden equipment
Colorable、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/XTWM206-BK1B069 |
|---|---|---|---|
| Dart impact | -30°C, Total Energy | ASTM D3763 | 3.00 J |
| 23°C, Total Energy | ASTM D3763 | 36.0 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/XTWM206-BK1B069 |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 100 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/XTWM206-BK1B069 |
|---|---|---|---|
| tensile strength | 屈服5 | ASTM D638 | 46.0 Mpa |
| elongation | 断裂5 | ASTM D638 | 26 % |
| Flexural modulus | 50.0 mm 跨距7 | ASTM D790 | 2450 Mpa |
| Tensile modulus | --4 | ASTM D638 | 2400 Mpa |
| --3 | ASTM D638 | 2360 Mpa | |
| elongation | 断裂 | ISO 527-2/50 | 36 % |
| 屈服6 | ASTM D638 | 2.5 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 36.0 Mpa |
| 屈服6 | ASTM D638 | 43.0 Mpa | |
| Flexural modulus | --8 | ISO 178 | 2380 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 45.0 Mpa |
| elongation | 屈服 | ISO 527-2/50 | 2.8 % |
| bending strength | --8,9 | ISO 178 | 64.0 Mpa |
| tensile strength | 断裂6 | ASTM D638 | 36.0 Mpa |
| elongation | 屈服5 | ASTM D638 | 2.7 % |
| bending strength | 屈服, 50.0 mm 跨距7 | ASTM D790 | 74.0 Mpa |
| tensile strength | 断裂5 | ASTM D638 | 37.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2350 Mpa |
| elongation | 断裂6 | ASTM D638 | 27 % |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/XTWM206-BK1B069 |
|---|---|---|---|
| gloss | 60°, 无织构 | ASTM D523 | 93 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/XTWM206-BK1B069 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/XTWM206-BK1B069 |
|---|---|---|---|
| melt mass-flow rate | 220°C/10.0 kg | ASTM D1238 | 8.8 g/10 min |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.20 % |
| Shrinkage rate | 流动 2 | 内部方法 | 0.40 - 0.70 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.40 - 0.75 % | |
| Outdoor applicability | UL 746C | f1 | |
| Melt volume flow rate | 260°C/5.0 kg | ISO 1133 | 9.00 cm3/10min |
| melt mass-flow rate | 280°C/3.8 kg | ASTM D1238 | 7.2 g/10 min |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.40 - 0.70 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.50 % |
| melt mass-flow rate | 260°C/5.0 kg | ASTM D1238 | 7.1 g/10 min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/XTWM206-BK1B069 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 8.4E-5 cm/cm/°C |
| vicat | -- | ISO 306/B120 | 99.0 °C |
| ball-indentation hardness | 83 到 87°C | IEC 60695-10-2 | 通过 |
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距11，HDT | ISO 75-2/Bf | 98.0 °C |
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 9.4E-5 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 95.0 °C |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ISO 11359-2 | 8.3E-5 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 97.0 °C |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 9.4E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距11，HDT | ISO 75-2/Af | 84.0 °C |
| vicat | -- | 98.0 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 84.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/XTWM206-BK1B069 |
|---|---|---|---|
| screw speed | 30 to 80 rpm | ||
| Suggested maximum moisture content | 0.040 % | ||
| Processing (melt) temperature | 240 to 270 °C | ||
| drying temperature | 85 to 90 °C | ||
| Suggested injection volume | 40 to 80 % | ||
| drying time | 4.0 hr | ||
| Temperature in the middle of the barrel | 220 to 255 °C | ||
| Temperature at the rear of the barrel | 215 to 250 °C | ||
| Exhaust hole depth | 0.038 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 230 to 260 °C | ||
| Back pressure | 0.300 to 1.00 Mpa | ||
| Temperature | 60 to 85 °C | ||
| Spray nozzle temperature | 220 to 255 °C |