PBT B4300G3 BASF MALAYSIA
Ultradur®
Engineering accessories、Shell、electrical machinery、printed circuit board
High rigidity、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF MALAYSIA/B4300G3 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃23℃ | ISO 179/1eU | 41 kJ/m² |
| Charpy Notched Impact Strength | 23℃23℃ | ISO 179/1eA | 5.5 kJ/m² |
| Supplementary Information | Test Condition | Test Method | BASF MALAYSIA/B4300G3 |
|---|---|---|---|
| Automotive Materials | > 1.00 mm> 1.00 mm | FMVSS 302 | Pass |
| Mechanical properties | Test Condition | Test Method | BASF MALAYSIA/B4300G3 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 6200 Mpa | |
| tensile strength | 断裂断裂 | ISO 527-2 | 100 Mpa |
| Tensile strain | 断裂断裂 | ISO 527-2 | 3.5 % |
| Electrical performance | Test Condition | Test Method | BASF MALAYSIA/B4300G3 |
|---|---|---|---|
| Dissipation Factor | 1 MHz1 MHz | IEC 60250 | 0.00037 |
| relative permittivity | 100 Hz100 Hz | IEC 60250 | 0.0012 |
| Dissipation Factor | 100 Hz100 Hz | IEC 60250 | 0.00037 |
| Electrical performance | 体积电阻率Volume Resistivity | IEC 60093 | 10000000000000 ohms·cm |
| relative permittivity | 1 MHz1 MHz | IEC 60250 | 0.015 |
| Flame retardant performance | Test Condition | Test Method | BASF MALAYSIA/B4300G3 |
|---|---|---|---|
| UL flame retardant rating | 0.80 mm | UL 94 | HB |
| 1.60 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | BASF MALAYSIA/B4300G3 |
|---|---|---|---|
| Shrinkage rate | MD：自由的free, longitudinal | 0.5 % | |
| Water absorption rate | 平衡，23℃，50% RHEquilibrium, 73°F, 50% RH | ISO 62 | 0.2 % |
| viscosity number | ISO 307 | 112 cm³/g | |
| Water absorption rate | 饱和，23℃Saturation, 73°F | ISO 62 | 0.4 % |
| Melt volume flow rate | 250℃，2.16 kg250℃/2.16 kg | ISO 1133 | 15 cm3/10min |
| density | ISO 1183 | 1.42 g/cm³ | |
| Shrinkage rate | TD：自由的free, transverse | 1.4 % |
| Thermal performance | Test Condition | Test Method | BASF MALAYSIA/B4300G3 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 223 °C | |
| maximum service temperature | short cycle operationshort cycle operation | 210 °C | |
| Heat distortion temperature | 0.45 MPa，未退火66 psi, Unannealed，HDT | ISO 75-2/B | 220 °C |
| 1.8 MPa，未退火264 psi, Unannealed，HDT | ISO 75-2/A | 200 °C | |
| Linear coefficient of thermal expansion | MD：23~80℃MD：23 到 80℃ | ISO 11359-2 | 0.000040 1/℃ |