PI, TP XH1005 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/XH1005 resin |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 21 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 43 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 20.7 J |
| Impact strength of cantilever beam gap | 23°C10 | ISO 180/1A | 4.4 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC/XH1005 resin |
|---|---|---|---|
| elongation | 断裂5 | ASTM D638 | 15 % |
| tensile strength | 屈服 | ISO 527-2/5 | 101 MPa |
| Flexural modulus | --7 | ISO 178 | 2850 MPa |
| tensile strength | 屈服5 | ASTM D638 | 103 MPa |
| bending strength | 屈服,50.0mm跨距6 | ASTM D790 | 168 MPa |
| Tensile modulus | -- | ISO 527-2/1 | 3160 MPa |
| elongation | 屈服 | ISO 527-2/5 | 6.0 % |
| bending strength | --7,8 | ISO 178 | 150 MPa |
| tensile strength | 断裂 | ISO 527-2/5 | 70.0 MPa |
| elongation | 屈服5 | ASTM D638 | 7.0 % |
| tensile strength | 断裂5 | ASTM D638 | 96.0 MPa |
| Tensile modulus | --4 | ASTM D638 | 3420 MPa |
| Flexural modulus | 50.0mm跨距6 | ASTM D790 | 3130 MPa |
| elongation | 断裂 | ISO 527-2/5 | 6.0 % |
| flammability | Test Condition | Test Method | SABIC/XH1005 resin |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC/XH1005 resin |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 1.0to1.2 % |
| density | ASTMD792 | 1.31 g/cm³ | |
| melt mass-flow rate | 367°C/6.6kg | ASTM D1238 | 6.0 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.0 % |
| 饱和,23°C | ISO 62 | 2.3 % | |
| 23°C,24hr3 | ASTM D570 | 0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC/XH1005 resin |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 237 °C |
| vicat | -- | ISO 306/B120 | 252 °C |
| Linear coefficient of thermal expansion | TD:23到150°C | ISO 11359-2 | 5.1E-05 cm/cm/°C |
| vicat | -- | ASTM D152512 | 260 °C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 250 °C |
| vicat | -- | ISO 306/B50 | 253 °C |
| Linear coefficient of thermal expansion | MD:23到150°C | ISO 11359-2 | 5E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 235 °C |
| 1.8MPa,未退火,64.0mm跨距11，HDT | ISO 75-2/Af | 225 °C |