PC/ABS XCM840－BK1005 SABIC INNOVATIVE US
CYCOLAC™
Automotive interior parts、Electrical applications
High mobility、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCM840－BK1005 |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 6.1E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 120 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 6.1E-05 cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 4.6E-05 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 120 °C |
| Vicat Softening Temperature | ISO306/B50 | 138 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 4.6E-05 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCM840－BK1005 |
|---|---|---|---|
| Flexural Modulus | ISO178 | 4000 Mpa | |
| Tensile Elongation | 屈服 | ASTMD638 | 4.0 % |
| Tensile Strain | 断裂 | ISO527-2/5 | 50 % |
| Tensile Modulus | ISO527-2/1 | 4300 Mpa | |
| Flexural Strength | ISO178 | 100 Mpa | |
| Tensile Modulus | ASTMD638 | 4300 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 56.0 Mpa |
| 断裂 | ASTMD638 | 47.0 Mpa | |
| Tensile Stress | 断裂 | ISO527-2/5 | 47.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/5 | 4.0 % |
| Tensile Stress | 屈服 | ISO527-2/5 | 56.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/XCM840－BK1005 |
|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Volume flow Rate | 265°C/5.0kg | ISO1133 | 12.7 cm3/10min |
| 260°C/5.0kg | ISO1133 | 10.0 cm3/10min | |
| Modeling Shrinkage | TD：3.20mm | 内部方法 | 0.50to0.70 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCM840－BK1005 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 8.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 11 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 60.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 37 kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 15 kJ/m² |