POM 127UV DUPONT USA
Delrin®
Medical supplies
High temperature resistan、Flame retardant、enhance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/127UV |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 15 kJ/m² |
| -30°C | ISO 179/1eA | 11 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 400 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 13 kJ/m² |
| -40°C | ISO 180/1A | 11 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 350 kJ/m² |
| hardness | Test Condition | Test Method | DUPONT USA/127UV |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
| M计秤 | ISO 2039-2 | 92 |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/127UV |
|---|---|---|---|
| Odor | VDA270 | 3.00 | |
| Emission | VDA275 | <8.00 mg/kg | |
| Emissions of Organic Compounds | VDA277 | 16.0 µgC/g |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/127UV |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3000 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 45 % | |
| bending strength | 3.5%Strain | ISO 178 | 80.5 Mpa |
| Flexural modulus | ISO 178 | 2700 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 23 % |
| bending strength | -- | ISO 178 | 72.0 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 70.0 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/127UV |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.50 |
| 1MHz | IEC 60250 | 3.40 |
| flammability | Test Condition | Test Method | DUPONT USA/127UV |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | IEC 60695-11-10,-20 | HB |
| Fogging-G-value | condensate | ISO 6452 | 1.5E-04 g |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| burning rate | 1.00mm | ISO 3795 | 28 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/127UV |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 1.90 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.9 % |
| MD | ISO 294-4 | 2.1 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 1.2 % |
| 23°C,24hr | ISO 62 | 0.50 % | |
| density | ISO 1183 | 1.42 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 2.4 g/10min |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.30 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/127UV |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 178 °C | |
| AnnealingTemperature | 160 °C | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 160 °C |
| vicat | ISO 306/B50 | 160 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 93.0 °C |
| AnnealingTime-Optional | 30.0 min/mm | ||
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.1E-04 cm/cm/°C |