Thermoset Premi-Glas® 3101-20 USA Premix
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | USA Premix/Premi-Glas® 3101-20 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 530 J/m |
| Mechanical properties | Test Condition | Test Method | USA Premix/Premi-Glas® 3101-20 |
|---|---|---|---|
| tensile strength | ASTM D638 | 33.0 MPa | |
| Tensile modulus | ASTM D638 | 13000 MPa | |
| Flexural modulus | ASTM D790 | 10300 MPa | |
| bending strength | ASTM D790 | 110 MPa | |
| Poisson's ratio | 0.30 |
| Electrical performance | Test Condition | Test Method | USA Premix/Premi-Glas® 3101-20 |
|---|---|---|---|
| dielectric strength | ASTM D149 | 18 kV/mm | |
| arc resistance | ASTM D495 | 210 sec |
| flammability | Test Condition | Test Method | USA Premix/Premi-Glas® 3101-20 |
|---|---|---|---|
| UL flame retardant rating | 2.6mm | UL 94 | 5V |
| 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | USA Premix/Premi-Glas® 3101-20 |
|---|---|---|---|
| density | 1.80to1.95 g/cm³ | ||
| Shrinkage rate | MD | 0.15to0.30 % |
| Thermal performance | Test Condition | Test Method | USA Premix/Premi-Glas® 3101-20 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | >200 °C |
| thermal conductivity | 0.30 W/m/K | ||
| Linear coefficient of thermal expansion | MD2 | 2.5E-05 cm/cm/°C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Str | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | TD3 | 3.5E-05 cm/cm/°C | |
| RTI Elec | UL 746 | 130 °C |