PBT 420SE0-8051 SABIC INNOVATIVE US

VALOX™

Office supplies,Electronic accessories

Glass fiber reinforced,high strength

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE US/420SE0-8051
Ball Pressure Test	H358/30	ISO 2039-1	118 Mpa
Rockwell hardness	R-Scale	ASTM D785	119
Rockwell hardness		R-Scale	ISO 2039-2	119

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/420SE0-8051
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	200 °C
		1.8MPa,Unannealed,100mmSpan9	ISO 75-2/Ae	195 °C
		0.45MPa,Unannealed,3.20mm	ASTM D648	212 °C
		1.8MPa,Unannealed,64.0mmSpan10	ISO 75-2/Af	200 °C
		0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	220 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	2.5E-05 cm/cm/°C
		TD：-40to40°C	ISO 11359-2	8.9E-05 cm/cm/°C
		TD：-40to40°C	ASTME831	8.9E-05 cm/cm/°C
		TD：23to80°C	ISO 11359-2	1.2E-04 cm/cm/°C
		MD：23to80°C	ISO 11359-2	2.5E-05 cm/cm/°C
		MD：-40to40°C	ISO 11359-2	2.5E-05 cm/cm/°C
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	130 °C
RTI Str		UL 746	140 °C
thermal conductivity		ISO 8302	0.25 W/m/K
Vicat softening temperature	--	ISO 306/B120	200 °C
		--	ISO 306/B50	200 °C
			ASTM D152511	200 °C
		--	ISO 306/A50	220 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/420SE0-8051
Bending modulus	50.0mmSpan	ASTM D790	9800 Mpa
Bending modulus			ISO 178	9500 Mpa
bending strength		ISO 178	180 Mpa
bending strength		Break,50.0mmSpan	ASTM D790	186 Mpa
elongation	Break	ASTM D638	2.0 %
elongation		Yield	ASTM D638	2.0 %
Taber abraser	1000Cycles,1000g,CS-17Wheel	Internal Method	22.0 mg
Tensile modulus		ASTM D638	12000 Mpa
Tensile modulus			ISO 527-2/1	10000 Mpa
Tensile strain	Break	ISO 527-2/5	1.9 %
Tensile strain		Yield	ISO 527-2/5	1.9 %
tensile strength	Break	ISO 527-2/5	120 Mpa
		Yield	ASTM D638	120 Mpa
		Yield	ISO 527-2/5	120 Mpa
		Break	ASTM D638	120 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE US/420SE0-8051
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI	UL 746	PLC 3
		SolutionB	IEC 60112	V
		--	IEC 60112	V
Dielectric constant	100Hz	ASTM D150	3.80
Dielectric constant		1MHz	ASTM D150	3.70
Dielectric strength	0.800mm,in Oil	IEC 60243-1	23 KV/mm
		3.20mm,in Oil	IEC 60243-1	16 KV/mm
		3.20mm,inAir	ASTM D149	19 KV/mm
		1.60mm,in Oil	IEC 60243-1	22 KV/mm
		1.60mm,in Oil	ASTM D149	24 KV/mm
Dissipation factor	1MHz	IEC 60250	0.010
		1MHz	ASTM D150	0.020
		60Hz	IEC 60250	1E-03
		50Hz	IEC 60250	1E-03
		100Hz	ASTM D150	2E-03
		100Hz	IEC 60250	2E-03
High arc combustion index	HAI	UL 746	PLC 0
High voltage arc tracing rate	HVTR	UL 746	PLC 4
Hot wire ignition	HWI	UL 746	PLC 2
Relative permittivity	100Hz	IEC 60250	3.80
		60Hz	IEC 60250	3.30
		1MHz	IEC 60250	3.30
		50Hz	IEC 60250	3.30
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Volume resistivity			ASTM D257	>1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/420SE0-8051
density		ISO 1183	1.63 g/cm³
density			ASTM D792	1.63 g/cm³
melt mass-flow rate	250°C/5.0kg	ASTM D1238	42 g/10min
Melt Volume Flow Rate (MVR)	250°C/5.0kg	ISO 1133	29.0 cm3/10min
Outdoor applicability		UL 746C	f2
Shrinkage rate	TD：--2	Internal Method	0.40-0.80 %
		TD：3.20mm	Internal Method	0.50-1.0 %
		MD：3.20mm	Internal Method	0.50-0.70 %
		MD：--2	Internal Method	0.10-0.50 %
Specific volume		ASTM D792	0.610 cm³/g
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.070 %
Water absorption rate		Saturation,23°C	ISO 62	0.090 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/420SE0-8051
Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.0 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	6.0 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	5.00 J
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.0 kJ/m²
		23°C	ISO 180/1A	7.0 kJ/m²
		23°C	ASTM D256	60 J/m
		23°C	ASTM D4812	620 J/m
		-30°C	ASTM D256	57 J/m
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	50 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	50 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	45 kJ/m²
Suspended wall beam without notch impact strength		-30°C	ISO 180/1U	45 kJ/m²

flammability	Test Condition	Test Method	SABIC INNOVATIVE US/420SE0-8051
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
Extreme Oxygen Index		ISO 4589-2	32 %
UL flame retardant rating	2.0mm	UL 94	5VA
		0.40mm	UL 94	V-2
		0.71mm	UL 94	V-0