Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC E2000UR MITSUBISHI THAILAND
IUPILON™
Automotive Applications、electrical equipment
Thermal stability、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | MITSUBISHI THAILAND/E2000UR |
|---|---|---|---|
| UL flame retardant rating | 1.60mm | UL 94 | V-2 |
| Basic performance | Test Condition | Test Method | MITSUBISHI THAILAND/E2000UR |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D-570 | 0.24 % |
| Shrinkage rate | MD,3.00mm | ASTM D-955 | 0.6 % |
| density | ASTM D-792 | 1.20 g/cm³ | |
| melt mass-flow rate | 300℃/1.2kg | ASTM D-1238 | 6.0 g/10min |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI THAILAND/E2000UR |
|---|---|---|---|
| Rockwell hardness | R | ASTM D-785 | 123 |
| Impact strength of cantilever beam gap | 3.20mm | ASTM D-256 | 1000 J/m |
| Flexural modulus | 3.20mm | ASTM D-790 | 2350 Mpa |
| tensile strength | 3.20mm | ASTM D-638 | 65.0 Mpa |
| bending strength | 3.20mm | ASTM D-790 | 90.0 Mpa |
| elongation | 断裂,3.20mm | ASTM D-638 | 120 % |
| Dart impact | 3.20mm | ASTM D-3029 | > 85.0 J |
| Electrical performance | Test Condition | Test Method | MITSUBISHI THAILAND/E2000UR |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 2.1E+16 ohm·cm | |
| dielectric constant | ASTM D150 | 2.85 |
| optical performance | Test Condition | Test Method | MITSUBISHI THAILAND/E2000UR |
|---|---|---|---|
| transmissivity | 总计, 3000 µm | ASTM D1003 | 85.0 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI THAILAND/E2000UR |
|---|---|---|---|
| vicat | ASTM D-1525 | 101 °C | |
| Linear coefficient of thermal expansion | 流动 | ASTM D-696 | 6.5E-05 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D-648 | 153 °C |
| 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D-648 | 138 °C |