PA6 OPTAMID® PA 6 G SCHWARTZ GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SCHWARTZ GERMANY/OPTAMID® PA 6 G |
|---|---|---|---|
| Impact strength of cantilever beam gap | kJ/m² | >3.7 >15 | |
| Suspended wall beam without notch impact strength | 无断裂 |
| hardness | Test Condition | Test Method | SCHWARTZ GERMANY/OPTAMID® PA 6 G |
|---|---|---|---|
| ball-indentation hardness | MPa | 150 120 |
| Electrical performance | Test Condition | Test Method | SCHWARTZ GERMANY/OPTAMID® PA 6 G |
|---|---|---|---|
| dielectric strength | kV/mm | 50 20 | |
| Dissipation Factor | 0.030 -- | ||
| Surface Resistivity | ohms | 1E+12 1E+10 | |
| dielectric constant | 3.70 -- |
| Mechanical properties | Test Condition | Test Method | SCHWARTZ GERMANY/OPTAMID® PA 6 G |
|---|---|---|---|
| tensile strength | 屈服 | MPa | 80.0 60.0 |
| 断裂 | MPa | 130 55.0 | |
| Tensile modulus | MPa | 3500 2700 | |
| coefficient of friction | 与钢-动态 | 0.040 0.080 | |
| 与钢-静态 | 0.35 0.42 | ||
| Flexural modulus | MPa | 3100 2400 | |
| Tensile strain | 断裂 | % | >25 -- |
| physical property | Test Condition | Test Method | SCHWARTZ GERMANY/OPTAMID® PA 6 G |
|---|---|---|---|
| density | g/cm³ | 1.15 -- | |
| Water absorption rate | 饱和,23°C | % | 7.0 -- |
| 23°C,24hr | % | 2.2 -- |
| Thermal performance | Test Condition | Test Method | SCHWARTZ GERMANY/OPTAMID® PA 6 G |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 210 -- |
| melting temperature | °C | 220 -- | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 120 -- |
| specific heat | J/kg/°C | 1670 -- | |
| thermal conductivity | W/m/K | 0.25 -- | |
| Linear coefficient of thermal expansion | MD：20到100°C | cm/cm/°C | 7.0E-5到8.0E-5 -- |