PC 1201-05 LG CHEM KOREA
LUPOY®
Toy,Food containers,chip,bottle
transparent,wear resistant,Low viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG CHEM KOREA/1201-05 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C, 3.18 mm | ASTM D256 | 950 J/m |
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 无断裂 |
| Dart impact | 23°C, 3.18 mm, Total Energy | ASTM D3763 | 94.0 J |
| hardness | Test Condition | Test Method | LG CHEM KOREA/1201-05 |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 74 |
| R 级 | ASTM D785 | 118 |
| thermal performance | Test Condition | Test Method | LG CHEM KOREA/1201-05 |
|---|---|---|---|
| Ball pressure temperature | IEC 60598-1 | > 125 °C | |
| Heat Deflection Temperature | 1.8 MPa, 退火, 4.00 mm，HDT | ASTM D648 | 143 °C |
| vicat | ASTM D15257 | 151 °C | |
| Heat Deflection Temperature | 0.45 MPa, 退火, 4.00 mm，HDT | ASTM D648 | 146 °C |
| 1.8 MPa, 未退火, 4.00 mm，HDT | ASTM D648 | 132 °C | |
| Linear coefficient of thermal expansion | -40 到 82°C，流动 | ASTM D696 | 6.8E-5 cm/cm/°C |
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/1201-05 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2410 Mpa | |
| elongation | 断裂 | ASTM D638 | 150 % |
| 屈服 | ASTM D638 | 6.0 % | |
| tensile strength | 断裂 | ASTM D638 | 72.0 Mpa |
| flexural modulus | ASTM D790 | 2410 Mpa | |
| tensile strength | 屈服, 23°C3 | ASTM D638 | 60.0 Mpa |
| bending strength | ASTM D790 | 96.0 Mpa | |
| wear resistance | Delta Haze | ASTM D1004 | 45 % |
| Electrical performance | Test Condition | Test Method | LG CHEM KOREA/1201-05 |
|---|---|---|---|
| dielectric constant | 60 Hz | ASTM D150 | 3.00 |
| Dissipation Factor | 60 Hz | ASTM D150 | 1.0E-3 |
| dielectric strength | ASTM D149 | 17 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | 2.00 mm | IEC 60112 | PLC 2 |
| volume resistivity | 23°C | ASTM D257 | 2.0E+17 ohms·cm |
| optical performance | Test Condition | Test Method | LG CHEM KOREA/1201-05 |
|---|---|---|---|
| transmissivity | ASTM D1003 | 89.0 % | |
| refractive index | ASTM D542 | 1.586 | |
| Haze ratio | ASTM D1003 | 0.70 to 1.5 % |
| Physical properties | Test Condition | Test Method | LG CHEM KOREA/1201-05 |
|---|---|---|---|
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 0.15 % |
| 平衡, 23°C, 50% RH | ASTM D570 | 0.32 % | |
| shrinkage rate | Flow | ASTM D955 | 0.50 - 0.70 % |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 5.0 g/10 min |
| density | ASTM D792 | 1.20 g/cm³ |
| flammability | Test Condition | Test Method | LG CHEM KOREA/1201-05 |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | HB |
| Hot filament ignition temperature | 2.0 mm, 5.0 sec | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 0.50 mm | UL 94 | V-2 |
| 1.6 mm | UL 94 | V-2 | |
| Average degree of combustion | ASTM D635 | 3 CM | |
| Limiting Oxygen Index | ASTM D2863 | 26 % | |
| UL flame retardant rating | 2.527mm | UL 94 | V-2 |