Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GSH2030KR 98410 MITSUBISHI ENGINEERING JAPAN
IUPILON™
Automotive Applications、electrical equipment
Glass fiber reinforced、Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2030KR 98410 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 34 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+10 Ω.cm |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2030KR 98410 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 175 Mpa |
| Flexural modulus | 23°C | ISO 178 | 8100 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 8700 Mpa |
| tensile strength | 23°C | ISO 527-2 | 116 Mpa |
| Flame retardant performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2030KR 98410 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 0.40mm | |
| UL -94 | HB 3.00mm |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2030KR 98410 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.09 % |
| Shrinkage rate | MD2.0mm | ISO 294-4 | 0.15 % |
| melt mass-flow rate | 300℃/1.2Kg | ISO 1133 | 5.50 cm3/10min |
| Shrinkage rate | TD2.0mm | ISO 294-4 | 0.35 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2030KR 98410 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 141 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 145 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 6.3E-05 cm/cm/°C |