PA66 RX07034 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and Electrical Applications,Lighting applications
Easy to form,Filler: Glass fiber reinf,40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/RX07034 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 86 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 18.0 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 4.00 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 16 kJ/m² |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/RX07034 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-30to30°C | ASTM D696 | 6.2E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 244 °C |
| 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 260 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 253 °C | |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 3.2E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 259 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RX07034 |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2/5 | 2.9 % |
| tensile strength | 断裂 | ISO 527-2/5 | 232 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 337 Mpa |
| Tensile modulus | ASTM D638 | 13900 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.9 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 12400 Mpa |
| tensile strength | 屈服 | ASTM D638 | 230 Mpa |
| bending strength | ISO 178 | 229 Mpa | |
| tensile strength | 屈服 | ISO 527-2/5 | 232 Mpa |
| Tensile modulus | ISO 527-2/1 | 14100 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/5 | 2.9 % |
| elongation | 屈服 | ASTM D638 | 2.8 % |
| tensile strength | 断裂 | ASTM D638 | 210 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 338 Mpa |
| flexural modulus | ISO 178 | 11200 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RX07034 |
|---|---|---|---|
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.66 % |
| shrinkage rate | MD：24小时 | ASTM D955 | 0.20-0.40 % |
| TD：24hr | ASTM D955 | 1.0-3.0 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.0 % |