LDPE LP 2427K LYONDELLBASELL SAUDI
LUPOLEN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | LYONDELLBASELL SAUDI/LP 2427K |
|---|---|---|---|
| Failure energy | 50.0µm | DIN 53373 | 35.0 J/cm |
| film | Test Condition | Test Method | LYONDELLBASELL SAUDI/LP 2427K |
|---|---|---|---|
| film thickness | 15to40µm | ||
| Dart impact | 50µm,吹塑薄膜 | ASTM D1709 | 100 g |
| elongation | MD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 300 % |
| tensile strength | TD:50µm,吹塑薄膜 | ISO 527-3 | 16.0 Mpa |
| elongation | TD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 600 % |
| tensile strength | MD:50µm,吹塑薄膜 | ISO 527-3 | 19.0 Mpa |
| Mechanical properties | Test Condition | Test Method | LYONDELLBASELL SAUDI/LP 2427K |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 260 Mpa | |
| coefficient of friction | 吹塑薄膜 | ISO 8295 | <0.20 |
| tensile strength | 屈服 | ISO 527-2 | 11.0 Mpa |
| optical performance | Test Condition | Test Method | LYONDELLBASELL SAUDI/LP 2427K |
|---|---|---|---|
| gloss | 20°,50.0µm,吹塑薄膜 | ASTM D2457 | >50 |
| Haze ratio | 50.0µm,吹塑薄膜 | ASTM D1003 | <9.0 % |
| gloss | 60°,50.0µm,吹塑薄膜 | ASTM D2457 | >100 |
| physical property | Test Condition | Test Method | LYONDELLBASELL SAUDI/LP 2427K |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 4.0 g/10min |
| Thermal performance | Test Condition | Test Method | LYONDELLBASELL SAUDI/LP 2427K |
|---|---|---|---|
| vicat | ISO 306/A50 | 92.0 °C | |
| melting temperature | ISO 3146 | 111 °C |