Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA D3WG12HMG BK00102 BASF SHANGHAI
Ultramid®
Alternative Metals
High rigidity、high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF SHANGHAI/D3WG12HMG BK00102 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 95 kJ/m² |
| 23°C | ISO 179 | 99 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF SHANGHAI/D3WG12HMG BK00102 |
|---|---|---|---|
| tensile strength | 断裂, 23°C | ISO 527-2 | 248 Mpa |
| Tensile strain | 断裂, 23°C | ISO 527-2 | 2.5 % |
| bending strength | 23°C | ISO 178 | 383 Mpa |
| Flexural modulus | 23°C | ISO 178 | 18900 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 20200 Mpa |
| physical property | Test Condition | Test Method | BASF SHANGHAI/D3WG12HMG BK00102 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.0 % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.19 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 2.5 % |
| Shrinkage rate | 横向流量 | ISO 294-4 | 0.25 % |
| Thermal performance | Test Condition | Test Method | BASF SHANGHAI/D3WG12HMG BK00102 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 224 °C |
| melting temperature | ISO 3146 | 260 °C |
| injection | Test Condition | Test Method | BASF SHANGHAI/D3WG12HMG BK00102 |
|---|---|---|---|
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.15 % | ||
| Injection Pressure | 3.50 to 12.5 Mpa | ||
| Processing (melt) temperature | 280 to 305 °C | ||
| drying temperature | 80 °C | ||
| Temperature | 80 to 90 °C | ||
| injection speed | 快速 |