PES Lapex A G/10 LATI S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | LATI S.p.A./Lapex A G/10 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 3.5 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
Supplementary Information | Test Condition | Test Method | LATI S.p.A./Lapex A G/10 |
---|---|---|---|
dimensional stability | 66.0 |
Mechanical properties | Test Condition | Test Method | LATI S.p.A./Lapex A G/10 |
---|---|---|---|
tensile strength | 断裂,90°C | ISO 527-2/5 | 90.0 MPa |
Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.5 % |
tensile strength | 断裂,120°C | ISO 527-2/5 | 75.0 MPa |
断裂,150°C | ISO 527-2/5 | 70.0 MPa | |
Tensile modulus | 90°C | ISO 527-2/1 | 4400 MPa |
Tensile strain | Yield,150°C | ISO 527-2/5 | 3.2 % |
Tensile modulus | 23°C | ISO 527-2/1 | 4600 MPa |
60°C | ISO 527-2/1 | 4500 MPa | |
Tensile strain | 断裂,120°C | ISO 527-2/5 | 4.4 % |
tensile strength | 断裂,60°C | ISO 527-2/5 | 95.0 MPa |
Tensile strain | 断裂,150°C | ISO 527-2/5 | 20 % |
tensile strength | 断裂,23°C | ISO 527-2/5 | 100 MPa |
Tensile modulus | 120°C | ISO 527-2/1 | 4300 MPa |
150°C | ISO 527-2/1 | 4100 MPa | |
Tensile strain | 断裂,60°C | ISO 527-2/5 | 3.7 % |
断裂,90°C | ISO 527-2/5 | 4.1 % | |
tensile strength | Yield,150°C | ISO 527-2/5 | 75.0 MPa |
flammability | Test Condition | Test Method | LATI S.p.A./Lapex A G/10 |
---|---|---|---|
UL flame retardant rating | 3.0mm | UL 94 | V-0 |
1.5mm | UL 94 | V-0 | |
Limiting Oxygen Index | ASTM D2863 | 39 % |
physical property | Test Condition | Test Method | LATI S.p.A./Lapex A G/10 |
---|---|---|---|
Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.40to0.55 % |
Water absorption rate | 23°C,24hr | ISO 62 | 0.18 % |
density | ISO 1183 | 1.45 g/cm³ | |
Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.60to0.80 % |
Thermal performance | Test Condition | Test Method | LATI S.p.A./Lapex A G/10 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 220 °C |
vicat | ISO 306/B50 | 220 °C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 215 °C |
Continuous use temperature | 180 °C | ||
Linear coefficient of thermal expansion | MD:30到100°C | ISO 11359-2 | 1.8E-05 cm/cm/°C |