PPO EXNL1137 BK1066 SABIC INNOVATIVE SHANGHAI
NORYL™
Instrument panel componen、Mechanical Engineering、valve
High temperature resistan、Hydrolysis resistance、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/EXNL1137 BK1066 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 16 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 34.2 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.8 kJ/m² |
| 23°C | ISO 180/1A | 16 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/EXNL1137 BK1066 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2910 Mpa | |
| elongation | 屈服 | ASTM D638 | 5.2 % |
| tensile strength | 断裂 | ASTM D638 | 51.3 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.9 % |
| tensile strength | 断裂 | ISO 527-2/50 | 53.3 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2630 Mpa |
| Tensile modulus | ASTM D638 | 2170 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 64.9 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 104 Mpa |
| elongation | 断裂 | ASTM D638 | 29 % |
| bending strength | ISO 178 | 107 Mpa | |
| Flexural modulus | ISO 178 | 2630 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 63.3 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 21 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/EXNL1137 BK1066 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.80 % |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 9.6 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.050 % |
| 饱和,23°C | ISO 62 | 0.25 % | |
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 9.85 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/EXNL1137 BK1066 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 138 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.1E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 7.4E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 136 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.4E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 7.1E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 116 °C |
| vicat | ASTM D152510 | 136 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 115 °C |