PC/ABS
PC/ABS SABIC INNOVATIVE NANSHA XCY620-100
Cold resistant grade
US$ 3,272 / MT
FOB Guangzhou port, China
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XCY620-100
elongationBreakASTM D638120 %
bending strengthISO 17883.0 Mpa
Bending modulus50.0mmSpanASTM D7902300 Mpa
Tensile modulusISO 527-2/12200 Mpa
ASTM D6382300 Mpa
tensile strengthBreakISO 527-2/5051.0 Mpa
YieldISO 527-2/5054.0 Mpa
Tensile strainBreakISO 527-2/50120 %
bending strengthYield,50.0mmSpanASTM D79089.0 Mpa
tensile strengthBreakASTM D63852.0 Mpa
YieldASTM D63855.0 Mpa
Bending modulusISO 1782200 Mpa
Tensile strainYieldISO 527-2/504.5 %
elongationYieldASTM D6384.7 %
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XCY620-100
Vicat softening temperature--ISO 306/B50127 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af105 °C
1.8MPa,Unannealed,3.20mmASTM D648107 °C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-27E-05 cm/cm/°C
MD：-40to40°CASTME8317E-05 cm/cm/°C
TD：-40to40°CASTME8317E-05 cm/cm/°C
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf126 °C
thermal conductivityISO 83020.20 W/m/K
Ball Pressure Test75°CIEC 60695-10-2Pass
Vicat softening temperature--ISO 306/B120129 °C
ASTM D152512127 °C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-27E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XCY620-100
Melt Volume Flow Rate (MVR)260°C/5.0kgISO 113318.0 cm3/10min
Shrinkage rateTD：3.20mmInternal Method0.50-0.70 %
melt mass-flow rate260°C/5.0kgASTM D123822 g/10min
MeltViscosity260°C,1500sec^-1ISO 11443195 Pa·s
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Water absorption rateSaturation,23°CISO 620.40 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XCY620-100
Dart impact-30°C,TotalEnergyASTM D376370.0 J
23°C,TotalEnergyASTM D376356.0 J
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/XCY620-100
Dielectric strength3.20mm,in OilIEC 60243-117 KV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Dielectric strength1.60mm,in OilIEC 60243-125 KV/mm
Surface resistivityIEC 60093>1.0E+15 ohms
Dielectric strength0.800mm,in OilIEC 60243-135 KV/mm