ASA/PC HRA150-BR8B018U SABIC INNOVATIVE US
GELOY™
Automotive sector、Outdoor applications
High temperature resistan、UV resistance、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HRA150-BR8B018U |
|---|---|---|---|
| Linear thermal expansion coefficient | MD：23到60°C | ISO11359-2 | 8E-05 cm/cm/°C |
| Thermal Conductivity | ISO8302 | 0.20 W/m/K | |
| RTIElec | UL746 | 50.0 °C | |
| Ball PressureTest | 105°C7 | IEC60695-10-2 | Pass |
| RTI | UL746 | 50.0 °C | |
| 0.45MPa, Unannealed,100mm Span | ISO75-2/Be | 125 °C | |
| Evolution Calendar intelligent importer | UL746 | 50.0 °C | |
| 1.8MPa, Unannealed,100mm Span | ISO75-2/Ae | 101 °C | |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/HRA150-BR8B018U |
|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 104 Mpa |
| Rockwell Hardness | R计秤 | ISO2039-2 | 118 |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HRA150-BR8B018U |
|---|---|---|---|
| fracture | ISO527-2/5 | 55.0 Mpa | |
| Flexural Modulus | ISO178 | 2400 Mpa | |
| fracture | ISO527-2/50 | >50 % | |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 125 mg |
| yield | ISO527-2/5,ISO527-2/50 | 4.0 % | |
| ISO527-2/5 | 55.0 Mpa | ||
| Tensile Modulus | ISO527-2/1 | 2500 Mpa | |
| fracture | ISO527-2/50 | 59.0 Mpa | |
| ISO527-2/5 | 120 % | ||
| Flexural Stress | ISO178 | 80.0 Mpa | |
| yield | ISO527-2/50 | 59.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/HRA150-BR8B018U |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.20 % |
| Melt Volume flow Rate | 260°C/5.0kg | ISO1133 | 15.0 cm3/10min |
| Modeling Shrinkage | MD1 | 内部方法 | 0.40到0.60 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.60 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HRA150-BR8B018U |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 kJ/m² |
| 23°C | ISO179/1eA | 65 kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 45 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HRA150-BR8B018U |
|---|---|---|---|
| Flame Rating | 3.00mm | UL94 | HB |
| Oxygen Index | ISO4589-2 | 20 % | |
| Glow Wire Flammability Index | 3.20mm | IEC60695-2-12 | 750 °C |
| Flame Rating | 0.750mm | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HRA150-BR8B018U |
|---|---|---|---|
| Dielectric Strength | 3.20mm,在油中 | IEC60243-1 | 17 KV/mm |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Comparative Tracking Index | IEC60112 | 175 V | |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Relative Permittivity | 1MHz | IEC60250 | 2.90 |
| Dissipation Factor? | 1MHz | IEC60250 | 0.015 |