Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 243R-111 SABIC INNOVATIVE CHONGQING
LEXAN™
Industrial applications、Automotive sector、Electrical appliances、Lighting applications、Plastic bag
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/243R-111 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 800 J/m |
| Falling hammer impact | 23°C | ASTMD3029 | 169 J |
| Tensile impact strength 4 | ASTMD1822 | 546 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ASTMD4812 | 3200 J/m |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/243R-111 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTMD785 | 70 |
| R计秤 | ASTMD785 | 118 |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/243R-111 |
|---|---|---|---|
| High arc combustion index (HAI) | HAI | UL746 | PLC 1 |
| Volume resistivity | ASTMD257 | >1.0E+17 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL746 | PLC 2 |
| dielectric constant | 50Hz | ASTMD150 | 3.17 |
| 1MHz | ASTMD150 | 2.96 | |
| 60Hz | ASTMD150 | 3.17 | |
| Hot wire ignition (HWI) | HWI | UL746 | PLC 4 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL746 | PLC 2 |
| Dissipation Factor | 50Hz | ASTMD150 | 9E-04 |
| dielectric strength | 3.20mm,inAir | ASTMD149 | 15 KV/mm |
| Dissipation Factor | 1MHz | ASTMD150 | 0.010 |
| 60Hz | ASTMD150 | 9E-04 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/243R-111 |
|---|---|---|---|
| elongation | 屈服 | ASTMD638 | 7.0 % |
| 断裂 | ASTMD638 | 110 % | |
| tensile strength | 屈服 | ASTMD638 | 62.1 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTMD790 | 93.1 Mpa |
| tensile strength | 断裂 | ASTMD638 | 65.5 Mpa |
| 1000Cycles,1000g,CS-17转轮 | ASTMD1044 | 10.0 mg | |
| Flexural modulus | 50.0mm跨距 | ASTMD790 | 2340 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/243R-111 |
|---|---|---|---|
| transmissivity | 2540µm | ASTMD1003 | 88.0 % |
| refractive index | ASTMD542 | 1.586 | |
| Haze ratio | 2540µm | ASTMD1003 | 1.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/243R-111 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | V-2 |
| Limiting Oxygen Index | ASTMD2863 | 25 % | |
| UL flame retardant rating | 6.0mm | UL94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/243R-111 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Water absorption rate | 平衡,23°C | ASTMD570 | 0.35 % |
| density | ASTMD792 | 1.20 g/cm³ | |
| Water absorption rate | 24hr | ASTMD570 | 0.15 % |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 11 g/10min |
| Water absorption rate | 平衡,100°C | ASTMD570 | 0.58 % |
| Outdoor applicability | UL746C | f1 | |
| Specific volume | ASTMD792 | 0.830 cm³/g |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/243R-111 |
|---|---|---|---|
| vicat | ASTMD15255 | 154 °C | |
| MD：-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C | |
| thermal conductivity | ASTMC177 | 0.27 W/m/K | |
| RTI Str | UL746 | 130 °C | |
| RTI Elec | UL746 | 130 °C | |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 132 °C |
| 0.45MPa,未退火,6.40mm | ASTMD648 | 138 °C | |
| RTI Imp | UL746 | 130 °C | |
| specific heat | ASTMC351 | 1260 J/kg/°C |