TP, Unspecified Ultralloy™ 910-5 HAPCO USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | HAPCO USA/Ultralloy™ 910-5 |
---|---|---|---|
Suspended wall beam without notch impact strength | ASTM D256 | 52 J/m | |
Impact strength of cantilever beam gap | ASTM D256 | 25 J/m |
hardness | Test Condition | Test Method | HAPCO USA/Ultralloy™ 910-5 |
---|---|---|---|
Shore hardness | 邵氏D | ASTM D2240 | 84 |
Mechanical properties | Test Condition | Test Method | HAPCO USA/Ultralloy™ 910-5 |
---|---|---|---|
elongation | 断裂 | ASTM D638 | 4.0 % |
tensile strength | ASTM D638 | 57.9 MPa | |
Flexural modulus | ASTM D790 | 2550 MPa | |
Tensile modulus | ASTM D638 | 2190 MPa | |
bending strength | ASTM D790 | 66.9 MPa |
thermosetting | Test Condition | Test Method | HAPCO USA/Ultralloy™ 910-5 |
---|---|---|---|
Thermosetting mixed viscosity | 25°C | ASTM D4878 | 550 cP |
GelTime | 25°C | ASTM D2971 | 3.5 min |
stripping time | 21°C | 内部方法 | 30to60 min |
Thermosetting components | 部件A | 按重量计算的混合比:100.按容量计算的混合比:100 | |
部件B | 按重量计算的混合比:95.按容量计算的混合比:100 |
flammability | Test Condition | Test Method | HAPCO USA/Ultralloy™ 910-5 |
---|---|---|---|
UL flame retardant rating | UL 94 | V-0 |
physical property | Test Condition | Test Method | HAPCO USA/Ultralloy™ 910-5 |
---|---|---|---|
Shrinkage rate | MD | ASTM D2566 | 0.20to0.60 % |
density | ASTM D4669 | 1.20 g/cm³ | |
Weight Percubicinch | 20 g |
Thermal performance | Test Condition | Test Method | HAPCO USA/Ultralloy™ 910-5 |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ASTM D648 | 107 °C |