PC LUX7436C-WH5E143X SABIC INNOVATIVE US

LEXAN™

Plastic bag,Lighting applications

Flame retardant

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/LUX7436C-WH5E143X
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	131 °C
		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	120 °C
		0.45 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Be	131 °C
		1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Ae	120 °C
Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.9E-5 cm/cm/°C
		Flow : -40 to 40°C	ASTM E831	6.7E-5 cm/cm/°C
		Across Flow : -40 to 40°C	ASTM E831	6.7E-5 cm/cm/°C
		Flow : 23 to 80°C	ISO 11359-2	7.7E-5 cm/cm/°C
RTI		UL 746	125 °C
RTI Elec		UL 746	125 °C
RTI Imp		UL 746	120 °C
Vicat softening temperature	--	ISO 306/B120	139 °C
		--	ISO 306/B50	137 °C
		--	ASTM D152510	136 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/LUX7436C-WH5E143X
Bending modulus	--5	ISO 178	2450 Mpa
Bending modulus		50.0 mm Span4	ASTM D790	2450 Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	107 Mpa
bending strength		--5,6	ISO 178	101 Mpa
elongation	Yield	ISO 527-2/50	6.0 %
		Yield3	ASTM D638	6.0 %
		Break3	ASTM D638	55 %
		Break	ISO 527-2/50	56 %
Tensile modulus	--2	ASTM D638	2520 Mpa
Tensile modulus		--	ISO 527-2/1	2350 Mpa
tensile strength	Yield	ISO 527-2/50	66.0 Mpa
		Break	ISO 527-2/50	53.0 Mpa
		Break3	ASTM D638	55.0 Mpa
		Yield3	ASTM D638	67.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE US/LUX7436C-WH5E143X
Dielectric constant	1.10 GHz	ASTM ES7-83	2.79
Dissipation factor	1.10 GHz	ASTM ES7-83	5.7E-3

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/LUX7436C-WH5E143X
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	10 g/10 min
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	9.00 cm3/10min
Outdoor applicability		UL 746C	f1
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.60 - 0.80 %
Shrinkage rate		Flow : 3.20 mm	Internal Method	0.55 - 0.75 %
Water absorption rate	Saturation, 23°C	ISO 62	0.13 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.10 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/LUX7436C-WH5E143X
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	7.0 kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	64.0 J
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	23°C	ASTM D4812	无断裂
Suspended wall beam without notch impact strength		-30°C	ASTM D4812	无断裂

flammability	Test Condition	Test Method	SABIC INNOVATIVE US/LUX7436C-WH5E143X
Burning wire flammability index	1.2 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.2 mm	IEC 60695-2-13	850 °C
UL flame retardant rating	3.0 mm	UL 94	5VA
		1.0 mm	UL 94	V-1
		0.40 mm	UL 94	V-2
		1.2 mm	UL 94	V-0

injection	Test Condition	Test Method	SABIC INNOVATIVE US/LUX7436C-WH5E143X
Back pressure			0.300 to 0.700 Mpa
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Exhaust hole depth			0.025 to 0.076 mm
Mold temperature			70 to 95 °C
Processing (melt) temperature			280 to 305 °C
Screw speed			40 to 70 rpm
Spray nozzle temperature			275 to 300 °C
Suggested injection volume			40 to 60 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			280 to 305 °C
Temperature at the rear of the barrel			260 to 280 °C
Temperature in the middle of the barrel			270 to 295 °C