Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 9B24300 4Plas
--
--
Improved impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | 4Plas/9B24300 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 600 V |
| Volume resistivity | IEC 60093 | 1E+15 ohm.cm | |
| Surface Resistivity | IEC 60093 | 1E+13 Ω.cm | |
| IEC 60093 | 1E+13 ohms | ||
| Volume resistivity | IEC 60093 | 1E+15 Ω.cm |
| Mechanical properties | Test Condition | Test Method | 4Plas/9B24300 |
|---|---|---|---|
| Tensile strain | 23℃，屈服 | ISO 527-2 | 5.0 % |
| Tensile modulus | 23°C | ISO 527-2 | 1500 MPa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 85 kJ/m² |
| Tensile modulus | 23℃ | ISO 527-2 | 1500 MPa |
| Tensile stress | 23℃ | ISO 527-2 | 45.0 MPa |
| Charpy Notched Impact Strength | 23℃ | 85 | |
| -30℃ | ISO 179/eU | 无断裂 KJ/m2 | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NB kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 25 kJ/m² |
| -30℃ | ISO 180/1A | 25.0 KJ/m2 | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 25 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 80 kJ/m² |
| Charpy Notched Impact Strength | -30℃ | ISO 179/eA | 25 KJ/m2 |
| Impact strength of cantilever beam gap | 23℃ | 80.0 | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NB kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 45 MPa |
| elongation at break | 23°C | ISO 527-2 | 5.0 % |
| Flame retardant performance | Test Condition | Test Method | 4Plas/9B24300 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.60mm | |
| UL -94 | HB 3.20mm |
| physical property | Test Condition | Test Method | 4Plas/9B24300 |
|---|---|---|---|
| density | ISO 1183 | 1.04 g/cm3 | |
| Water absorption rate | 饱和,23℃ | ISO 62 | 8.0 % |
| (23°C,24hr) | ISO 62 | 8.00 % | |
| 平衡,23℃,50%RH | 2.3 | ||
| Shrinkage rate | 橫向流量 | ISO 294-4 | 1.5 % |
| MD2.0mm | ISO 294-4 | 1.50 % | |
| density | ISO 1183 | 1.04 g/cm³ | |
| Water absorption rate | (23°C,50RH) | ISO 62 | 2.30 % |
| Shrinkage rate | TD2.0mm | ISO 294-4 | 1.50 % |
| Thermal performance | Test Condition | Test Method | 4Plas/9B24300 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 50 °C |
| melting temperature | DSC法 | ISO 3146 | 223 ℃ |
| UL flame retardant rating | 1.60mm | UL 94 | HB |
| vicat | 熔融温度 | ISO 11357-3 | 223 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 50.0 |