Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL1330 BK1114 SABIC INNOVATIVE US
LEXAN™ 
sporting goods,Aerospace Applications,Electrical appliances,Plastic bag
Middle flow,Ductility at low temperat,Short molding cycle
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 BK1114
Ball Pressure TestH 358/30ISO 2039-190.0 Mpa
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 BK1114
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D648134 °C
1.8 MPa, Unannealed, 3.20 mmASTM D648120 °C
0.45 MPa, Unannealed, 4.00 mm, 100 mm Span10ISO 75-2/Be136 °C
1.8 MPa, Unannealed, 4.00 mm, 100 mm Span10ISO 75-2/Ae125 °C
1.8 MPa, Unannealed, 6.40 mmASTM D648124 °C
Linear coefficient of thermal expansionAcross Flow : 23 to 80°CISO 11359-27.2E-5 cm/cm/°C
Flow : -40 to 40°CASTM E8316.7E-5 cm/cm/°C
Across Flow : -40 to 40°CASTM E8316.7E-5 cm/cm/°C
Flow : 23 to 80°CISO 11359-27.2E-5 cm/cm/°C
RTIUL 746120 °C
RTI ElecUL 746125 °C
RTI ImpUL 746115 °C
Vicat softening temperature--ISO 306/B120145 °C
--ASTM D152511143 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 BK1114
Bending modulus--5ISO 1782100 Mpa
50.0 mm Span4ASTM D7902060 Mpa
bending strengthYield, 50.0 mm Span4ASTM D79088.0 Mpa
--5,6ISO 17885.0 Mpa
elongationYieldISO 527-2/505.0 %
Yield3ASTM D6386.0 %
Break3ASTM D638130 %
BreakISO 527-2/50> 100 %
Tensile modulus--2ASTM D6382100 Mpa
--ISO 527-2/12100 Mpa
tensile strengthYieldISO 527-2/5055.0 Mpa
BreakISO 527-2/5056.0 Mpa
Break3ASTM D63861.0 Mpa
Yield3ASTM D63858.0 Mpa
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 BK1114
melt mass-flow rate300°C/1.2 kgASTM D123810 g/10 min
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 11339.00 cm3/10min
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.40 - 0.80 %
Flow : 3.20 mmInternal Method0.40 - 0.80 %
Water absorption rateSaturation, 23°CISO 620.35 %
Equilibrium, 23°C, 50% RHISO 620.15 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 BK1114
Charpy Notched Impact Strength23°CISO 179/1eA75 kJ/m²
-30°CISO 179/1eA60 kJ/m²
Dart impact23°C, Total EnergyASTM D376352.0 J
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
23°CISO 180/1U无断裂
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 BK1114
Burning wire flammability index0.8 mmIEC 60695-2-12850 °C
1.0 mmIEC 60695-2-12960 °C
Extreme Oxygen IndexISO 4589-235 %
Hot filament ignition temperature3.0 mmIEC 60695-2-13875 °C
1.0 mmIEC 60695-2-13875 °C
UL flame retardant rating0.8 mmUL 94HB
injectionTest ConditionTest MethodSABIC INNOVATIVE US/EXL1330 BK1114
Back pressure0.300 to 0.700 Mpa
drying temperature120 °C
drying time3.0 to 4.0 hr
Exhaust hole depth0.025 to 0.076 mm
Mold temperature70 to 95 °C
Processing (melt) temperature295 to 315 °C
Screw speed40 to 70 rpm
Spray nozzle temperature290 to 310 °C
Suggested injection volume40 to 60 %
Suggested maximum moisture content0.020 %
Temperature at the front of the material cylinder295 to 315 °C
Temperature at the rear of the barrel215 to 295 °C
Temperature in the middle of the barrel280 to 305 °C