Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO 731S-111 SABIC INNOVATIVE SHANGHAI
NORYL™
Food containers
High mobility、Antistatic、High temperature resistan、currency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/731S-111 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 15 kJ/m² |
| -30°C | ISO 179/1eA | 5.0 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
| 23°C | ISO 180/1A | 15 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/731S-111 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| bending strength | ISO 178 | 75.0 Mpa | |
| Flexural modulus | ISO 178 | 2200 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 30 % |
| 屈服 | ISO 527-2/50 | 5.0 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 50.0 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/731S-111 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.060 % |
| Melt volume flow rate | 280°C/5.0 kg | ISO 1133 | 8.00 cm3/10min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.23 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/731S-111 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 140 °C |
| Linear coefficient of thermal expansion | 横向 : 23 到 80°C | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 7.0E-5 cm/cm/°C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDT | ISO 75-2/Ae | 115 °C |
| vicat | -- | ISO 306/B50 | 135 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/731S-111 |
|---|---|---|---|
| drying time | 2.0 to 3.0 hr | ||
| Temperature in the middle of the barrel | 260 to 280 °C | ||
| Temperature at the rear of the barrel | 240 to 260 °C | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| Hopper temperature | 60 to 80 °C | ||
| drying temperature | 100 to 120 °C | ||
| Temperature at the front of the material cylinder | 280 to 300 °C | ||
| Temperature | 80 to 120 °C | ||
| Spray nozzle temperature | 260 to 280 °C |