Certificates
ASA KR2858G3 BASF GERMANY
Luran®S
Application in the automo
heat-resisting、High rigidity、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | BASF GERMANY/KR2858G3 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 170 Mpa |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/KR2858G3 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 6600 Mpa | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.5 % |
| bending strength | ISO 178 | 140 Mpa | |
| tensile strength | 屈服,23°C | ISO 527-2 | 110 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 2.5 % |
| physical property | Test Condition | Test Method | BASF GERMANY/KR2858G3 |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.40-0.70 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.30 % |
| 饱和,23°C | ISO 62 | 1.4 % | |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 5.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/KR2858G3 |
|---|---|---|---|
| vicat | -- | ISO 306/A50 | 120 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 110 °C |
| vicat | -- | ISO 306/B50 | 115 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 115 °C |