| film | Test Condition | Test Method | USA Chevron Phillips/mPact® D139FK |
|---|---|---|---|
| Dart impact | 25µm,吹塑薄膜 | ASTM D1709 | 600 g |
| Elmendorf tear strength | TD:25µm,吹塑薄膜 | ASTM D1922 | 440 g |
| tensile strength | TD:屈服,25µm,吹塑薄膜 | ASTM D882 | 9.65 MPa |
| Elmendorf tear strength | MD:25µm,吹塑薄膜 | ASTM D1922 | 230 g |
| tensile strength | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 57.2 MPa |
| Initial sealing temperature | 25µm,吹塑薄膜 | ASTMF88 | 102 °C |
| elongation | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 560 % |
| Secant modulus | 1%正割,MD:25µm,吹塑薄膜 | ASTM D882 | 165 MPa |
| film thickness | 25 µm | ||
| tensile strength | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 45.9 MPa |
| MD:屈服,25µm,吹塑薄膜 | ASTM D882 | 12.8 MPa | |
| elongation | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 450 % |
| Secant modulus | 1%正割,TD:25µm,吹塑薄膜 | ASTM D882 | 188 MPa |
| Mechanical properties | Test Condition | Test Method | USA Chevron Phillips/mPact® D139FK |
|---|---|---|---|
| coefficient of friction | 吹塑薄膜 | ASTM D1894 | 0.15 |
| optical performance | Test Condition | Test Method | USA Chevron Phillips/mPact® D139FK |
|---|---|---|---|
| Haze ratio | 25.4µm,吹塑薄膜 | ASTM D1003 | 9.0 % |
| gloss | 60°,25.4µm,吹塑薄膜 | ASTM D2457 | 103 |
| physical property | Test Condition | Test Method | USA Chevron Phillips/mPact® D139FK |
|---|---|---|---|
| density | ASTM D1505 | 0.918 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.0 g/10min |