Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS A512 XO2 TORAY JAPAN
Torelina®
engineering application ,Phone,Automotive components,battery
Thermal stability,Filler: Carbon fiber rein,10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/A512 XO2 |
|---|---|---|---|
| Wear factor | vs.SUS | SuzukiMethod | 0.500 mg/hr |
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.5 % |
| bending strength | 23°C | ISO 178 | 156 Mpa |
| Wear factor | vs.S45C | SuzukiMethod | 0.200 mg/hr |
| coefficient of friction | vs.S45C | SuzukiMethod | 0.15 |
| vs.SUS | SuzukiMethod | 0.060 | |
| Flexural modulus | 23°C | ISO 178 | 9400 Mpa |
| tensile strength | 23°C | ISO 527-2 | 110 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/A512 XO2 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 10 ohms·cm |
| flammability | Test Condition | Test Method | TORAY JAPAN/A512 XO2 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/A512 XO2 |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.80 % |
| limiting pv value | vs.SUS | SuzukiMethod | 2.0 MPa·m/s |
| vs.S45C | SuzukiMethod | 2.9 MPa·m/s | |
| Shrinkage rate | MD:3.00mm3 | 内部方法 | 0.20 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/A512 XO2 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 260 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.1E-05 cm/cm/°C |
| melting temperature | DSC | 278 °C |