Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS AG15E3 FORMOSA NINGBO
TAIRILAC®
Electrical appliances、Electronic field、Electrical field
High gloss、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | FORMOSA NINGBO/AG15E3 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTMD256 | 150 J/m |
| 23°C,6.35mm | ISO180 | 150 J/m |
| hardness | Test Condition | Test Method | FORMOSA NINGBO/AG15E3 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTMD785 | 111 |
| R计秤,23°C | ISO2039-2 | 111 |
| Mechanical properties | Test Condition | Test Method | FORMOSA NINGBO/AG15E3 |
|---|---|---|---|
| Flexural modulus | 23°C | ASTMD790 | 2750 Mpa |
| 23°C | ISO178 | 2750 Mpa | |
| Bending stress | 23°C | ISO178 | 78.0 Mpa |
| tensile strength | 23°C | ASTMD638 | 48.0 Mpa |
| Tensile stress | 屈服,23°C | ISO527-2 | 48.0 Mpa |
| bending strength | 23°C | ASTMD790 | 78.0 Mpa |
| flammability | Test Condition | Test Method | FORMOSA NINGBO/AG15E3 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm,AllColors | UL94 | HB |
| physical property | Test Condition | Test Method | FORMOSA NINGBO/AG15E3 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.40to0.70 % |
| density | 23°C | ISO1183 | 1.05 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTMD1238 | 2.1 g/10min |
| 200°C/5.0kg | ISO1133 | 2.1 g/10min | |
| density | ASTMD792 | 1.05 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ISO1133 | 21 g/10min |
| 220°C/10.0kg | ASTMD1238 | 21 g/10min |
| Thermal performance | Test Condition | Test Method | FORMOSA NINGBO/AG15E3 |
|---|---|---|---|
| 1.8MPa,未退火,12.7mm | ASTMD648 | 86.0 °C | |
| vicat | ASTMD15253 | 103 °C | |
| 1.8MPa,Annealed | ASTMD648 | 96.0 °C | |
| vicat | ISO306/A | 103 °C | |
| 1.8MPa,Unannealed,12.7mm | ISO75-2/A | 86.0 °C | |
| 1.8MPa,退火 | ISO75-2/A | 96.0 °C |