Certificates
PA66 U4820L NC01 INVISTA SHANGHAI
INVISTA™
Electrical field、Electronic field、Automotive sector、Household appliances、Household appliances、currency
Processability、currency、Lubricity、Fast forming cycle、Color stability、Good demolding performanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | INVISTA SHANGHAI/U4820L NC01 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| -30°C | ISO 179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | INVISTA SHANGHAI/U4820L NC01 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3200 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 82.0 Mpa |
| bending strength | ISO 178 | 96.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 35 % |
| Flexural modulus | ISO 178 | 3000 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 4.1 % |
| Electrical performance | Test Condition | Test Method | INVISTA SHANGHAI/U4820L NC01 |
|---|---|---|---|
| dielectric strength | 1.00mm | IEC 60243-1 | 32 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | V |
| Surface Resistivity | IEC 60093 | 3E+14 ohms | |
| Volume resistivity | 2.00mm | IEC 60093 | 4E+14 ohms·cm |
| flammability | Test Condition | Test Method | INVISTA SHANGHAI/U4820L NC01 |
|---|---|---|---|
| Burning wire flammability index | 0.71mm | IEC 60695-2-12 | 960 °C |
| 3.0mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 0.71mm | IEC 60695-2-13 | 960 °C |
| 3.0mm | IEC 60695-2-13 | 750 °C | |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 900 °C |
| UL flame retardant rating | 0.40mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | INVISTA SHANGHAI/U4820L NC01 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 1.8 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 1.7 % |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 1.8 % |
| Thermal performance | Test Condition | Test Method | INVISTA SHANGHAI/U4820L NC01 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 262 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 221 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 71.0 °C |